Polymer Property : Flexural Strength = 111 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Flexural Strength 111 MPa
16100 psi
ASTM D790
Plaskolite Optix® CA-81 General Purpose Acrylic Resin
Extrusion Grade Pellets. Highest Molecular weight.
Flexural Strength 111 MPa
16100 psi
ASTM D790
Plaskolite West Optix® CA-81 General Purpose Acrylic Resin
Extrusion Grade Pellets. Highest Molecular weight.
Flexural Strength 111 MPa
16100 psi
ISO 178
Nilit FRIANYL A63 HH-FK 1020 Nylon 6.6 for injection molding, 10% glass fiber and 20% glass ball reinforced
Nylon 6.6 for injection moldingInformation provided by Frisetta Polymer, which merged into Nilit Plastics
Flexural Strength 111 MPa
16100 psi
Quadrant EPP Nylatron® GSM PA 6 + MoS2, cast (ISO Data)
Nylatron GSM contains finely divided particles of molybdenum disulphide to enhance its bearing and wear behaviour without impairing the impact and fatigue resistance inherent to unmodified cast nylo..
Flexural Strength 111 MPa

@Temperature 150 °C
16100 psi

@Temperature 302 °F
ISO 178
Solvay Specialty Polymers Amodel® A-1145 HS Polyphthalamide (PPA)  (Unverified Data**)
Amodel A-1145 HS is a 45% glass reinforced, heat stabilized polyphthalamide (PPA) with a high heat deflection temperature, very high flexural modulus and very high tensile strength. Excellent creep ..
Flexural Strength 111 MPa

@Temperature 150 °C
16100 psi

@Temperature 302 °F
ISO 178
Solvay Specialty Polymers Amodel® AS-4133 HS Polyphthalamide (PPA)  (Unverified Data**)
Amodel AS-4133 HS is a 33% glass reinforced, lubricated, heat stabilized grade of polyphthalamide (PPA) that offers fast cycle times and moldability in hot water molds. Typical applications include ..
Flexural Strength 111 MPa
16100 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP DFL42 PC
LNP* Lubricomp* DFL-4042 a compound based on Polycarbonate resin containing 10% Glass Fiber, 20% PTFE. Added features include: Internally Lubricated.
Flexural Strength 111 MPa
16100 psi
ASTM D790
Glastic BMC SLC-1000 Glass-Reinforced Polyester
Data provided by Glastic Corporation.Medium strength, V-0, adjustable shrinkage.
Flexural Strength 111 MPa
16100 psi
2 mm/min; ISO 178
Ineos ABS Lustran® SAN C Injection Molding Grade
Flexural Strength 111 MPa

@Temperature 150 °C
16100 psi

@Temperature 302 °F
4; ISO 178
Solvay Specialty Polymers Amodel® A-1145 HS Polyphthalamide (PPA), 45% Glass Fiber (Dry)
Amodel® A-1145 HS is a 45% glass reinforced, heat stabilized polyphthalamide (PPA) with a high heat deflection temperature, very high flexural modulus and very high tensile strength. Excellent cr..
Flexural Strength 111 MPa

@Temperature 150 °C
16100 psi

@Temperature 302 °F
4; ISO 178
Solvay Specialty Polymers Amodel® AS-4133 HS Polyphthalamide (PPA), 33% Glass Fiber (Dry)
Amodel® AS-4133 HS is a 33% glass reinforced, lubricated, heat stabilized grade of polyphthalamide (PPA) that offers fast cycle times and moldability in hot water molds. Testing conducted on samp..
Flexural Strength 111 MPa
16100 psi
2 mm/min; ISO 178
SABIC Innovative Plastics LNP STAT-KON DFD02EXC PC (Europe-Africa-Middle East)
LNP* Stat-kon* DFD02EXC is a compound based on Polycarbonate resin containing Glass Fiber, Carbon Powder. Added features of this material include: Electrically Conductive.
Flexural Strength 111 MPa
16100 psi
ISO 178
SABIC Innovative Plastics LNP Thermocomp IF002 PA 6/12 (Asia Pacific)
LNP* Thermocomp* IF002 is a compound based on Nylon 6/12 resin containing Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region.
Flexural Strength 111 MPa
16100 psi
2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP RKN14 PA 66 (Europe-Africa-Middle East)
LNP* Lubricomp* RKN14 is a compound based on Nylon 66 resin containing Mineral, MOS2.
Flexural Strength 111 MPa
16100 psi
2 mm/min; ISO 178
SABIC Innovative Plastics LNP STAT-KON DX92002 PC (Europe-Africa-Middle East)
LNP* Stat-kon* DX92002 is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive.
Flexural Strength 111 MPa
16100 psi
ASTM D790
SABIC Innovative Plastics Xenoy® X6320 PBT+PC (Asia Pacific)
X6320 is a mineral filled PBT/PC resin developed for automotive painted doorhandles. Key advantages are excellent surface finish, easy processing and paint quality.
Flexural Strength 111 MPa
16100 psi
ISO 178
SABIC Innovative Plastics LNP Thermocomp IF002 PA 6/12
LNP* Thermocomp* IF002 is a compound based on Nylon 6/12 resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region.
Flexural Strength 111 MPa
16100 psi
ASTM D 790
RTP Company RTP 1400 Polyethersulfone (PES)
Flexural Strength 111 MPa
16100 psi
ASTM D790
Unitika PT-3020
Characteristics: Dimensional accuracy (planarity) Heat resistance Creep resistance and elasticity RigidityInformation provided by Unitika Ltd.
Flexural Strength 111 MPa
16100 psi
ISO 178
Unitika TERRAMAC HV-6250H Polylactic Acid (PLA)
Foam, Extrusion, blow, and foam sheet grades. Bio-based materials produced from annually renewable raw materials.Information provided by Unitika Ltd.
Flexural Strength 111 MPa

@Temperature 22.8 °C
16100 psi

@Temperature 73.0 °F
ASTM D790
Celanese Celanex® 602AC PBT, Glass Reinforced
Celanex 602AC is a 10% fiberglass reinforced PBT that has lower warpage and improved impact over standard PBT.To avoid hydrolytic degradation during processing, CELANEX resins have to be dried to a ..
Flexural Strength 111 MPa
16100 psi
ASTM D790
A. Schulman ComAlloy Lubrilon® 604 Nylon 6/6, PTFE/Molybdenum Disulfide Filled, Flow Enhanced
Data provided by the manufacturer, ComAlloy International Company. High performance and excellent lubricity with minimal surface wear.The ComAlloy product line has been integrated into the A Schulma..
Flexural Strength 111 MPa
16100 psi
ISO 178
Denka TX-100S Transparent Resin Polymer (MS resin) Methyl Methacrylate Styrene
"TX Polymer" (methyl methacrylate styrene), MS resins as an alternative to acrylic resins, with low density, low moisture absorption, and good moldability, "TH Polymer/TP Polymer," MBS resins with a..
Flexural Strength 111 MPa

@Temperature 150 °C
16100 psi

@Temperature 302 °F
ISO 178
Solvay Specialty Polymers Amodel® AS-4133 HN Polyphthalamide (PPA), Dry, 33% Glass Fiber Reinforcement, Heat Stabilizer
Amodel AS-4133 HN polyphthalamide (PPA) is a non-lubricated, heat stabilized grade that offers fast cycle times and is hot-water moldable. Typical applications include electrical and electronic comp..
Flexural Strength 111 MPa
16100 psi
2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOTUF WF003I PBT (Europe-Africa-Middle East)
LNP* Thermotuf* WF003I BLACK is a compound based on Polybutylene Terephalate resin containing Glass Fiber. Added features of this material include: High Impact.
Flexural Strength 111 MPa
16100 psi
ASTM D 790
RTP Company RTP 1400 N Polyethersulfone (PES) High Viscosity