Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Stress | 240 MPa @Strain 2.00 % |
34800 psi @Strain 2.00 % |
|
Solvay TECHNYL® A 218 V50 PA66, 50% glass fiber, DRY Description: TECHNYL® A 218 V50 is a polyamide 66, reinforced with 50% of glass fiber, heat stabilized, for injection molding. This product is available in natural and black colors.Benefits: The .. |
|||
Tensile Stress | 240 MPa @Diameter 105 - 200 mm, Strain 0.200 % |
34800 psi @Diameter 4.13 - 7.87 in, Strain 0.200 % |
|
United Cast Bar Unibar 400-15 As Cast Continuously Cast Spheroidal Graphite Iron Offers superior machinability combined with good impact, fatigue, electrical conductivity and magnetic permeability. Noise and vibration damping are good in this grade.Unibar 400-15 is not recommend.. |
|||
Tensile Stress | 240 MPa @Diameter 205 - 600 mm, Strain 0.200 % |
34800 psi @Diameter 8.07 - 23.6 in, Strain 0.200 % |
|
United Cast Bar Unibar 400-15 As Cast Continuously Cast Spheroidal Graphite Iron Offers superior machinability combined with good impact, fatigue, electrical conductivity and magnetic permeability. Noise and vibration damping are good in this grade.Unibar 400-15 is not recommend.. |
|||
Tensile Stress | 240 MPa @Diameter 105 - 200 mm, Strain 0.200 % |
34800 psi @Diameter 4.13 - 7.87 in, Strain 0.200 % |
|
United Cast Bar Unibar 400-15 Fully Annealed Continuously Cast Spheroidal Graphite Iron Offers superior machinability combined with good impact, fatigue, electrical conductivity and magnetic permeability. Noise and vibration damping are good in this grade.Unibar 400-15 is not recommend.. |
|||
Tensile Stress | 240 MPa @Diameter 205 - 600 mm, Strain 0.200 % |
34800 psi @Diameter 8.07 - 23.6 in, Strain 0.200 % |
|
United Cast Bar Unibar 400-15 Fully Annealed Continuously Cast Spheroidal Graphite Iron Offers superior machinability combined with good impact, fatigue, electrical conductivity and magnetic permeability. Noise and vibration damping are good in this grade.Unibar 400-15 is not recommend.. |
|||
Tensile Stress | 240 MPa @Strain 0.500 %, Temperature 982 °C |
34800 psi @Strain 0.500 %, Temperature 1800 °F |
|
COI Ceramics Sylramic™ S200 Silicon Carbide Ceramic Matrix Composite, CG Nicalon Engineered ceramic composite structure.Reinforcing Fiber Flexibility: S400 - Carbon Preceramic Polymer Matrix Precursors: S400 - Crystalline (SiC + Si3N4) or SiCPhysical Attributes: Dense Matrix ( |