United Cast Bar Unibar 400-15 As Cast Continuously Cast Spheroidal Graphite Iron

Category Metal , Ferrous Metal , Cast Iron , Gray Cast Iron
Manufacturer United Cast Bar
Trade Name Unibar
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF United Cast Bar Unibar 400-15 As Cast Continuously Cast Spheroidal Graphite Iron.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Offers superior machinability combined with good impact, fatigue, electrical conductivity and magnetic permeability. Noise and vibration damping are good in this grade.Unibar 400-15 is not recommended for Hardening and Tempering.Information provided by United Cast Bar Ltd.
Physical Properties Metric English Comments
Density 7.30 g/cc
0.264 lb/in³
Mechanical Properties Metric English Comments
Hardness, Brinell 140 - 190

@Load 3000 kg
140 - 190

@Load 6610 lb
10 mm ball
Tensile Strength 370 MPa

@Diameter 105 - 200 mm
53700 psi

@Diameter 4.13 - 7.87 in
370 MPa

@Diameter 205 - 600 mm
53700 psi

@Diameter 8.07 - 23.6 in
390 MPa

@Diameter 55.0 - 100 mm
56600 psi

@Diameter 2.17 - 3.94 in
400 MPa

@Diameter 25.0 - 50.0 mm
58000 psi

@Diameter 0.984 - 1.97 in
Tensile Stress 240 MPa

@Diameter 105 - 200 mm,
Strain 0.200 %
34800 psi

@Diameter 4.13 - 7.87 in,
Strain 0.200 %
240 MPa

@Diameter 205 - 600 mm,
Strain 0.200 %
34800 psi

@Diameter 8.07 - 23.6 in,
Strain 0.200 %
250 MPa

@Diameter 25.0 - 50.0 mm,
Strain 0.200 %
36300 psi

@Diameter 0.984 - 1.97 in,
Strain 0.200 %
250 MPa

@Diameter 55.0 - 100 mm,
Strain 0.200 %
36300 psi

@Diameter 2.17 - 3.94 in,
Strain 0.200 %
Elongation at Break 11 %

@Thickness 105 - 200 mm
11 %

@Thickness 4.13 - 7.87 in
11 %

@Thickness 205 - 600 mm
11 %

@Thickness 8.07 - 23.6 in
14 %

@Thickness 55.0 - 100 mm
14 %

@Thickness 2.17 - 3.94 in
15 %

@Thickness 25.0 - 50.0 mm
15 %

@Thickness 0.984 - 1.97 in
Component Elements Properties Metric English Comments
Carbon, C 3.25 - 3.7 %
3.25 - 3.7 %
Iron, Fe 92.83 - 94.19 %
92.83 - 94.19 %
as balance
Magnesium, Mg 0.040 - 0.070 %
0.040 - 0.070 %
Manganese, Mn 0.10 - 0.30 %
0.10 - 0.30 %
Phosphorous, P 0.015 - 0.080 %
0.015 - 0.080 %
Silicon, Si 2.4 - 3.0 %
2.4 - 3.0 %
Sulfur, S 0.0050 - 0.020 %
0.0050 - 0.020 %