Polymer Property : Impact Test = 65.1 J Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Impact Test	65.1 J @Thickness 3.17 mm, Temperature -40.0 °C	48.0 ft-lb @Thickness 0.125 in, Temperature -40.0 °F	ARM impact
A. Schulman POLYAXIS® CP812 Stabilized Compounded Rotational Molding Resin DescriptionPolyaxis CP 812 is a stabilized compounded rotational molding resin with a combination of good flow and stiffness. NOTE: Physical properties are based on rotationally molded samples from ..
Impact Test	65.1 J @Thickness 3.17 mm, Temperature -40.0 °C	48.0 ft-lb @Thickness 0.125 in, Temperature -40.0 °F	ARM impact
A. Schulman POLYAXIS® CP812 Stabilized Compounded Rotational Molding Resin DescriptionPolyaxis CP 812 is a stabilized compounded rotational molding resin with a combination of good flow and stiffness. NOTE: Physical properties are based on rotationally molded samples from ..
Impact Test	65.1 J @Thickness 3.17 mm, Temperature -40.0 °C	48.0 ft-lb @Thickness 0.125 in, Temperature -40.0 °F	ARM impact
A. Schulman POLYAXIS® CP812 Stabilized Compounded Rotational Molding Resin DescriptionPolyaxis CP 812 is a stabilized compounded rotational molding resin with a combination of good flow and stiffness. NOTE: Physical properties are based on rotationally molded samples from ..
Impact Test	65.1 J @Thickness 3.17 mm, Temperature -40.0 °C	48.0 ft-lb @Thickness 0.125 in, Temperature -40.0 °F	ARM impact
A. Schulman POLYAXIS® CP812 Stabilized Compounded Rotational Molding Resin DescriptionPolyaxis CP 812 is a stabilized compounded rotational molding resin with a combination of good flow and stiffness. NOTE: Physical properties are based on rotationally molded samples from ..
Impact Test	65.1 J @Thickness 3.17 mm, Temperature -40.0 °C	48.0 ft-lb @Thickness 0.125 in, Temperature -40.0 °F	ARM impact
A. Schulman POLYAXIS® CP812 Stabilized Compounded Rotational Molding Resin DescriptionPolyaxis CP 812 is a stabilized compounded rotational molding resin with a combination of good flow and stiffness. NOTE: Physical properties are based on rotationally molded samples from ..
Impact Test	65.1 J @Thickness 3.17 mm, Temperature -40.0 °C	48.0 ft-lb @Thickness 0.125 in, Temperature -40.0 °F	ARM impact
A. Schulman POLYAXIS® CP812 Stabilized Compounded Rotational Molding Resin DescriptionPolyaxis CP 812 is a stabilized compounded rotational molding resin with a combination of good flow and stiffness. NOTE: Physical properties are based on rotationally molded samples from ..