Mechanical Properties	Metric	English	Comments
Impact Test	56.9 J @Thickness 3.17 mm, Temperature -40.0 °C	42.0 ft-lb @Thickness 0.125 in, Temperature -40.0 °F	ARM impact
A. Schulman POLYAXIS® LP624 Stabilized High Density Polyethylene DescriptionPolyaxis CP 624 is a stabilized high density polyethylene rotational molding compound with good flow and stiffness. NOTE: Physical properties are based on rotationally molded samples from..
Impact Test	56.9 J @Thickness 3.17 mm, Temperature -40.0 °C	42.0 ft-lb @Thickness 0.125 in, Temperature -40.0 °F	ARM impact
A. Schulman POLYAXIS® LP624 Stabilized High Density Polyethylene DescriptionPolyaxis CP 624 is a stabilized high density polyethylene rotational molding compound with good flow and stiffness. NOTE: Physical properties are based on rotationally molded samples from..
Impact Test	56.9 J @Thickness 3.17 mm, Temperature -40.0 °C	42.0 ft-lb @Thickness 0.125 in, Temperature -40.0 °F	ARM impact
A. Schulman POLYAXIS® LP624 Stabilized High Density Polyethylene DescriptionPolyaxis CP 624 is a stabilized high density polyethylene rotational molding compound with good flow and stiffness. NOTE: Physical properties are based on rotationally molded samples from..
Impact Test	56.9 J @Thickness 3.17 mm, Temperature -40.0 °C	42.0 ft-lb @Thickness 0.125 in, Temperature -40.0 °F	ARM impact
A. Schulman POLYAXIS® LP624 Stabilized High Density Polyethylene DescriptionPolyaxis CP 624 is a stabilized high density polyethylene rotational molding compound with good flow and stiffness. NOTE: Physical properties are based on rotationally molded samples from..
Impact Test	56.9 J @Thickness 3.17 mm, Temperature -40.0 °C	42.0 ft-lb @Thickness 0.125 in, Temperature -40.0 °F	ARM impact
A. Schulman POLYAXIS® LP624 Stabilized High Density Polyethylene DescriptionPolyaxis CP 624 is a stabilized high density polyethylene rotational molding compound with good flow and stiffness. NOTE: Physical properties are based on rotationally molded samples from..
Impact Test	56.9 J @Thickness 3.17 mm, Temperature -40.0 °C	42.0 ft-lb @Thickness 0.125 in, Temperature -40.0 °F	ARM impact
A. Schulman POLYAXIS® LP624 Stabilized High Density Polyethylene DescriptionPolyaxis CP 624 is a stabilized high density polyethylene rotational molding compound with good flow and stiffness. NOTE: Physical properties are based on rotationally molded samples from..