Polymer Property : 300% Modulus = 0.0156 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
300% Modulus	0.0156 GPa	2.26 ksi	aged 70 hours at 250ºF in ASTM Oil #901
TSE Industries Millathane® 5004 Millable Polyurethane Elastomer with 20 PHR HAF Black (Typical) MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c..
300% Modulus	0.0156 GPa	2.26 ksi	ASTM D412
Styron SprintanÂ® SLR 4601 Solution Styrene Butadiene Rubber (S-SBR) Composition: SPRINTANÂ® SLR-4601 â€“ Schkopau is manufactured by anionic solution polymerization using an organo-lithium initiator. The product has a medium styrene/high vinyl micro structure a..
300% Modulus	0.0156 GPa	2.26 ksi	aged 70 hours at 250ºF in ASTM Oil #901
TSE Industries Millathane® 5004 Millable Polyurethane Elastomer with 20 PHR HAF Black (Typical) MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c..
300% Modulus	0.0156 GPa @Temperature 145 °C, Time 2990 sec	2.26 ksi @Temperature 293 °F, Time 0.830 hour	cured; ASTM D412
LG Chemical NBR 6850 High Acrylonitrile Polymer Description: NBR 6850 is a copolymer of butadiene and acrylonitrile manufactured by advanced emulsion polymerization technology of Goodyear and LG Chem. NBR 6850 is a non staining, medium mooney, an..