Polymer Property : 300% Modulus = 0.0113 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
300% Modulus	0.0113 GPa	1.64 ksi	Injection molded parts; DIN 53504
Huntsman IROGRANÂ® A 85 P 5350 TPU-Polyester Introduction: IROGRAN A 85 P 5350 is a flame-retardant, halogen-free, polyether based thermoplastic polyurethane intended for extrusion and injection molding applications. IROGRAN A 85 P 5350 is par..
300% Modulus	0.0113 GPa	1.64 ksi	Cured
KKPC Kumho KHS 65 High Styrene Resin Masterbatch (HSR) High Styrene Resin Masterbatch (HSR)Characteristics: KOSYN KHS is produced by mixing SBR 1502 of 23.5% styrene and high styrene resin latex at high temperature. It works as plasticizer which improve..
300% Modulus	0.0113 GPa	1.64 ksi	Cured
KKPC Kumho KHS 65P High Styrene Resin Masterbatch (HSR) High Styrene Resin Masterbatch (HSR)Characteristics: KOSYN KHS is produced by mixing SBR 1502 of 23.5% styrene and high styrene resin latex at high temperature. It works as plasticizer which improve..
300% Modulus	0.0113 GPa	1.64 ksi	Cured
KKPC Kumho RM 21L High Styrene Resin Masterbatch (HSR) High Styrene Resin Masterbatch (HSR)Characteristics: KOSYN KHS is produced by mixing SBR 1502 of 23.5% styrene and high styrene resin latex at high temperature. It works as plasticizer which improve..
300% Modulus	0.0113 GPa	1.64 ksi
Taiwan Sheen Soon SheenthaneÂ® A8230 Thermoplastic Polyurethane Elastomer Thermoplastic polyurethane elastomer for injection moldingInformation provided by Taiwan Sheen Soon Co., LTD.
300% Modulus	0.0113 GPa	1.64 ksi	ASTM D412
Styron SprintanÂ® SLR 6430 Solution Styrene Butadiene Rubber (S-SBR) Composition: SPRINTANÂ® SLR-6430 â€“ Schkopau is manufactured by anionic solution polymerization using an organo-lithium initiator. In relation to solid rubber the grade is extended with 37.5 p..