KKPC Kumho KHS 65P High Styrene Resin Masterbatch (HSR)

Category Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE)
Manufacturer Korea Kumho Petrochemical Co., Ltd.
Trade Name Kumho
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF KKPC Kumho KHS 65P High Styrene Resin Masterbatch (HSR).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High Styrene Resin Masterbatch (HSR)Characteristics: KOSYN KHS is produced by mixing SBR 1502 of 23.5% styrene and high styrene resin latex at high temperature. It works as plasticizer which improves processability in rubber compounding, and has superior abrasion resistance, tear resistance and flex crack resistance. Also, it can hold up good physical properties with fillers. This product has superior compounding dispersibility and processability in addition to promoting the stiffness of manufactured goods.Applications: High solidity shoe part, foam sponge, equipment of automobile and other industrial tires.Additional Notes: Bound Styrene: 65%Stabilizer: Non-StainingAppearance: Pop-corn TypeCured Rubber: Press cured 50 minutes at 145°CThis product is so sensitive to sunlight and humidity that it can be tarnished and caused deterioration of quality if exposed. It is recommended to store it in cool and shady area lest it should be exposed to direct sunlight. Do not expose to incompatible materials or contaminants.Data provided by Korea Kumho Petrochemical Co., Ltd.
Physical Properties Metric English Comments
Density 1.00 g/cc
0.0361 lb/in³
Not Compounded
Mooney Viscosity 46

@Temperature 100 °C
46

@Temperature 212 °F
Compounded; ML1+4
61

@Temperature 100 °C
61

@Temperature 212 °F
Raw; ML1+4
Mechanical Properties Metric English Comments
Hardness, Shore A 95
95
Cured
Tensile Strength, Ultimate 13.7 MPa
1990 psi
Cured
Elongation at Break 400 %
400 %
Cured
300% Modulus 0.0113 GPa
1.64 ksi
Cured