Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Adhesive Bond Strength	7.58 MPa	1100 psi	Lap shear, alum to alum, 4 hrs @ 25°C + 2 hrs @ 65°C
Tra-Con Tra-Cast 3110 Low Density Epoxy Casting System TRA-CAST 3110 is a unicellular, low density, syntactic-foam epoxy resin casting system of medium viscosity that easily handles, mixes and cures at room temperature. Developed for industrial encapsul..
Adhesive Bond Strength	7.58 MPa	1100 psi	Lap shear, alum to alum, 24 hrs @ 25°C
Tra-Con Tra-Bond 216H02 Opaque Black Epoxy Casting Compound TRA-CAST 216H02 is a medium viscosity two-part formulation recommended for general purpose electrical potting and encapsulation applications where the combination of good mechanical thermal and elec..
Adhesive Bond Strength	7.58 MPa	1100 psi	Lap shear, alum to alum, 15 min @ 100°C
Tra-Con Tra-Bond 723C01 One-Part Medical Grade Adhesive TRA-BOND 723C01 is a fast, heat curing, one component adhesive targeted at medical applications. The material complies with USP Class VI toxicity requirements and is resistant to gamma sterilization..
Adhesive Bond Strength	7.58 MPa @Temperature 82.2 °C	1100 psi @Temperature 180 °F	Aluminum-Aluminum tensile shear
Armstrong C-1/H20 Epoxy Adhesive A versatile, low viscosity, unfilled resin used for electrical potting and laminating applications. It is an excellent insulator, and provides outstanding chemical resistance to most compoundsInfor..
Adhesive Bond Strength	7.58 MPa	1100 psi	Al-to-Al Lap Shear; Cured 1 hr at 25ºC; ASTM D1002
Aptek 6513-A/B Versatile, fast set adhesive APTEK 6513-A/B is a hazy clear, two component, general purpose, semi-rigid, paste adhesive for bonding to steel, aluminum, wood, concrete, glass, ceramics, bras, and a variety of plastics. It is sp..
Adhesive Bond Strength	7.58 MPa	1100 psi	Lap shear; 2024 T3 Al Abraded / MEK Wipe; TM R050-37
Resinlab® EP1296 Highly Filled, Moderately Thixotropic Black Casting Resin Resinlab™ EP1296 is a highly filled, moderately thixotropic black casting resin designed for applications requiring good thermal conductivity, low shrinkage and a low CTE. It was especially formula..