Polymer Property : Modulus of Elasticity = 29900 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Modulus of Elasticity	206 GPa	29900 ksi
Industeel SOLEIL C5 13% Cr 4 Ni Martensitic Stainless Steel with Improved Toughness Description: Soleil C5 is a 13% Cr 4 Ni 0.5 Mo martensitic stainless steel. Its nickel content, associated with low carbon ensures better weldability, ductility, impact resistance and fatigue resist..
Modulus of Elasticity	206 GPa @Temperature 400 Â°C	29900 ksi @Temperature 752 Â°F
Haynes 242Â® alloy Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815Â°C, excellent low cycle fatigue properties, very good therm..
Modulus of Elasticity	206 GPa @Temperature 400 Â°C	29900 ksi @Temperature 752 Â°F
Haynes 242Â® alloy, after 4000 hours exposure at 650Â°C (1200Â°F) Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815Â°C, excellent low cycle fatigue properties, very good therm..
Modulus of Elasticity	206 GPa @Temperature 400 Â°C	29900 ksi @Temperature 752 Â°F
Haynes 242Â® alloy, after 8000 hours exposure at 650Â°C (1200Â°F) Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815Â°C, excellent low cycle fatigue properties, very good therm..
Modulus of Elasticity	206 GPa @Temperature 400 Â°C	29900 ksi @Temperature 752 Â°F
Haynes 242Â® alloy, bar and rings, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815Â°C, excellent low cycle fatigue properties, very good therm..
Modulus of Elasticity	206 GPa @Temperature 400 Â°C	29900 ksi @Temperature 752 Â°F
Haynes 242Â® alloy, cold reduced sheet, annealed and 20% cold work Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815Â°C, excellent low cycle fatigue properties, very good therm..
Modulus of Elasticity	206 GPa @Temperature 400 Â°C	29900 ksi @Temperature 752 Â°F
Haynes 242Â® alloy, cold reduced sheet, annealed and 40% cold work Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815Â°C, excellent low cycle fatigue properties, very good therm..
Modulus of Elasticity	206 GPa @Temperature 400 Â°C	29900 ksi @Temperature 752 Â°F
Haynes 242Â® alloy, cold rolled sheet, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815Â°C, excellent low cycle fatigue properties, very good therm..
Modulus of Elasticity	206 GPa	29900 ksi	heat-treated at 1121Â°C (2050Â°F), rapid quenched, plate
Haynes HastelloyÂ® C-22Â® alloy, 0% cold worked sheet HASTELLOYÂ® C-22Â® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an..
Modulus of Elasticity	206 GPa	29900 ksi	heat-treated at 1121Â°C (2050Â°F), rapid quenched, plate
Haynes HastelloyÂ® C-22Â® alloy, 12.7-50.8 mm thick bar, solution heat treated HASTELLOYÂ® C-22Â® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an..
Modulus of Elasticity	206 GPa	29900 ksi	heat-treated at 1121Â°C (2050Â°F), rapid quenched, plate
Haynes HastelloyÂ® C-22Â® alloy, 20% cold worked sheet HASTELLOYÂ® C-22Â® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an..
Modulus of Elasticity	206 GPa	29900 ksi	heat-treated at 1121Â°C (2050Â°F), rapid quenched, plate
Haynes HastelloyÂ® C-22Â® alloy, 20% cold worked sheet, aged 100 hours at 500Â°C HASTELLOYÂ® C-22Â® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an..
Modulus of Elasticity	206 GPa	29900 ksi	heat-treated at 1121Â°C (2050Â°F), rapid quenched, plate
Haynes HastelloyÂ® C-22Â® alloy, 30% cold worked sheet HASTELLOYÂ® C-22Â® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an..
Modulus of Elasticity	206 GPa	29900 ksi	heat-treated at 1121Â°C (2050Â°F), rapid quenched, plate
Haynes HastelloyÂ® C-22Â® alloy, 40% cold worked sheet HASTELLOYÂ® C-22Â® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an..
Modulus of Elasticity	206 GPa	29900 ksi	heat-treated at 1121Â°C (2050Â°F), rapid quenched, plate
Haynes HastelloyÂ® C-22Â® alloy, 60% cold worked sheet, aged 100 hours at 500Â°C HASTELLOYÂ® C-22Â® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an..
Modulus of Elasticity	206 GPa	29900 ksi	heat-treated at 1121Â°C (2050Â°F), rapid quenched, plate
Haynes HastelloyÂ® C-22Â® alloy, all-weld metal, GMAW short arc HASTELLOYÂ® C-22Â® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an..
Modulus of Elasticity	206 GPa	29900 ksi	heat-treated at 1121Â°C (2050Â°F), rapid quenched, plate
Haynes HastelloyÂ® C-22Â® alloy, GTAW weld, C-22 base metal, C-22 weld metal HASTELLOYÂ® C-22Â® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an..
Modulus of Elasticity	206 GPa	29900 ksi	heat-treated at 1121Â°C (2050Â°F), rapid quenched, plate
Haynes HastelloyÂ® C-22Â® alloy, GTAW, aged 4000 hours at 450Â°C (800Â°F), notched HASTELLOYÂ® C-22Â® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an..
Modulus of Elasticity	206 GPa	29900 ksi	heat-treated at 1121Â°C (2050Â°F), rapid quenched, plate
Haynes HastelloyÂ® C-22Â® alloy, GTAW, as welded, notched HASTELLOYÂ® C-22Â® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an..
Modulus of Elasticity	206 GPa	29900 ksi	heat-treated at 1121Â°C (2050Â°F), rapid quenched, plate
Haynes HastelloyÂ® C-22Â® alloy, SMAW weld, 316L base metal, C-22 weld metal HASTELLOYÂ® C-22Â® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an..
Modulus of Elasticity	206 GPa	29900 ksi	heat-treated at 1121Â°C (2050Â°F), rapid quenched, plate
Haynes HastelloyÂ® C-22Â® alloy, SMAW weld, C-22 base metal, C-22 weld metal HASTELLOYÂ® C-22Â® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an..
Modulus of Elasticity	206 GPa	29900 ksi	heat-treated at 1121Â°C (2050Â°F), rapid quenched, plate
Haynes HastelloyÂ® C-22Â® alloy, transverse, GMAW spray weldment, 23.4 mm thick plate HASTELLOYÂ® C-22Â® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an..
Modulus of Elasticity	206 GPa	29900 ksi	heat-treated at 1121Â°C (2050Â°F), rapid quenched, plate
Haynes HastelloyÂ® C-22Â® alloy, transverse, GTAW weldment, sheet - plate HASTELLOYÂ® C-22Â® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an..
Modulus of Elasticity	206 GPa @Temperature 400 °C	29900 ksi @Temperature 752 °F
Haynes 242® alloy, hot rolled plate, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good thermal..
Modulus of Elasticity	206 GPa	29900 ksi	heat-treated at 1121°C (2050°F), rapid quenched, plate
Haynes Hastelloy® C-22® alloy, GTAW weld, 904L base metal, C-22 weld metal HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al..
Modulus of Elasticity	206 GPa	29900 ksi	heat-treated at 1121°C (2050°F), rapid quenched, plate
Haynes Hastelloy® C-22® alloy, transverse, GTAW spray weldment, 12.7 mm (1/2 in.) thick plate HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al..
Modulus of Elasticity	206 GPa	29900 ksi	heat-treated at 1121°C (2050°F), rapid quenched, plate
Haynes Hastelloy® C-22® alloy, 0% cold worked sheet, aged 100 hours at 500°C HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al..
Modulus of Elasticity	206 GPa	29900 ksi	heat-treated at 1121°C (2050°F), rapid quenched, plate
Haynes Hastelloy® C-22® alloy, 60% cold worked sheet HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al..
Modulus of Elasticity	206 GPa	29900 ksi	heat-treated at 1121°C (2050°F), rapid quenched, plate
Haynes Hastelloy® C-22® alloy, GTAW weld, 316L base metal, C-22 weld metal HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al..