Mechanical Properties	Metric	English	Comments
Modulus of Elasticity	197 GPa	28500 ksi	Tension
Latrobe LescalloyÂ® 15-5 VAC-ARC Precipitation Hardening Stainless Steel LESCALLOY 15-5 VAC-ARC steel is a precipitation hardening martensitic stainless steel commonly considered to be a compositional modification of 17-4 with minimal delta ferrite. A wide range of mec..
Modulus of Elasticity	197 GPa	28500 ksi	Tension
Latrobe LescalloyÂ® 17-4 VAC-ARC Precipitation Hardening Stainless Steel LESCALLOY 17-4 VAC-ARC steel is a precipitation hardening martensitic stainless steel. A wide range of mechanical properties is available via simple aging within a 900-1150Â°F (482-621Â°C) tempe..
Modulus of Elasticity	197 GPa	28500 ksi
Latrobe LSSâ„¢ 17-4 Precipitation Hardening Stainless Steel (ASTM Type 360) TLS 17-4 is a precipitation hardening, martensitic stainless steel that exhibits excellent resistance to atmospheric and chemical corrosion. TLS 17-4 exhibits an excellent combination of high stren..
Modulus of Elasticity	197 GPa	28500 ksi
Schmolz + Bickenbach UGIMA 303 UXÂ® Stainless Steel Bar Description: 303 UGIMA UXÂ® is an improved machining grade produced only by Ugitech, providing the ultimate level of machinability available in an austenitic stainless steel. 303 UGIMA UXÂ® feat..
Modulus of Elasticity	197 GPa	28500 ksi
Schmolz + Bickenbach UGIMAÂ® 303 HD Stainless Steel Bar Description: 303 UGIMA HDâ„¢ is a low sulfur version of Ugitechâ€™s improved machining 303 grade. It is designed to provide better metallurgical performance with respect to weldability, corros..
Modulus of Elasticity	197 GPa	28500 ksi	Tension; H900
Crucible Steel 15-5 Precipitation Hardening Stainless Steel Crucible 15-5 is a Premium Quality precipitation-hardening stainless steel which is capable of high strength and hardness levels after a relatively simple heat-treatment procedure. This grade is a V..
Modulus of Elasticity	197 GPa	28500 ksi	Tension; H900
Crucible Steel 17Cr-4Ni Precipitation Hardening Stainless Steel Crucible 17Cr-4Ni is a precipitation-hardening stainless steel which is capable of a high strength and hardness levels after a relatively simple heat-treatment procedure. This grade is martensitic a..
Modulus of Elasticity	197 GPa	28500 ksi	Tension; H900
Crucible Steel 17Cr-4Ni Super-X® Precipitation Hardening Stainless Steel Crucible 17Cr-4Ni is a version of 17CR-4Ni which has been modified to substantially improve machinability and other properties. Patented 17Cr-4Ni Super-X meets industry specifications for 17Cr-4Ni. ..
Modulus of Elasticity	197 GPa	28500 ksi
Crucible Steel CSM® 21 17Cr-4Ni Precipitation Hardening Stainless Steel CSM 21 is a precipitation hardening stainless mold steel, providing outstanding corrosion resistance and toughness, good polishability, and moderate wear resistance, combined with simple heat treatm..
Modulus of Elasticity	197 GPa	28500 ksi
Carlson 330 Austenitic Alloy General DescriptionCarlson Alloy 330 is a nickel-iron-chromium-silicon austenitic alloy. It combines high strength with excellent resistance to carburization and oxidation at temperatures to 2200°..
Modulus of Elasticity	197 GPa	28500 ksi
Carlson C 800 Nickel-Iron-Chromium Alloy General DescriptionCarlson Alloy C 800 is a nickel-iron-chromium alloy, combining high strength with excellent resistance to oxidation and carburization at elevated temperatures. This alloy resists..
Modulus of Elasticity	197 GPa	28500 ksi
Carlson C 800AT Nickel-Iron-Chromium Alloy General DescriptionCarlson Alloy C 800AT is a modification of Carlson Alloy C 800, exhibiting higher creep and rupture strengths. This nickel-iron-chromium alloy has a carbon content restricted to ..
Modulus of Elasticity	197 GPa	28500 ksi
Carlson C 800H Nickel-Iron-Chromium Alloy General DescriptionCarlson Alloy C 800 is a nickel-iron-chromium alloy, combining high strength with excellent resistance to oxidation and carburization at elevated temperatures. This alloy resists..