Material Notes:
General DescriptionCarlson Alloy 330 is a nickel-iron-chromium-silicon austenitic alloy. It combines high strength with excellent resistance to carburization and oxidation at temperatures to 2200°F (1200°C).330 remains completely austenitic at all temperatures; and is totally immune to sigma phase formations.With a 34 to 37 percent nickel content, 330 is highly resistant to chloride stress corrosion cracking. This high temperature alloy is often utilized for applications where conventional austenitic stainless steels are marginal.Applications330 is used extensively in elevated temperature environments where resistance to the combined effects of thermal cycling and carburization is required.Furnace Containers – annealing, carbonitriding, malleablizing.Heat Treating Equipment – muffles, retorts, conveyor systems, baskets, boxes, quenching fixtures.Gas Turbine ComponentsHeat ExchangersFurnace FansPetrochemical Furnace PartsSalt Pots – neutral, cyanideHot Pressing Platens.Information provided by Carlson
Physical Properties Metric English Comments
Density 7.97 g/cc
0.288 lb/in³
Mechanical Properties Metric English Comments
Tensile Strength at Break >= 483 MPa
>= 70000 psi
Tensile Strength, Yield >= 207 MPa

@Strain 0.200 %
>= 30000 psi

@Strain 0.200 %
Elongation at Break >= 30 %
>= 30 %
Modulus of Elasticity 197 GPa
28500 ksi
Thermal Properties Metric English Comments
CTE, linear 17.5 µm/m-°C

@Temperature 21.1 - 816 °C
9.70 µin/in-°F

@Temperature 70.0 - 1500 °F
18.0 µm/m-°C

@Temperature 21.1 - 982 °C
10.0 µin/in-°F

@Temperature 70.0 - 1800 °F
Specific Heat Capacity 0.460 J/g-°C
0.110 BTU/lb-°F
Melting Point 1340 - 1390 °C
2450 - 2540 °F
Solidus 1340 °C
2450 °F
Liquidus 1390 °C
2540 °F
Component Elements Properties Metric English Comments
Carbon, C <= 0.080 %
<= 0.080 %
Chromium, Cr 17 - 20 %
17 - 20 %
Copper, Cu <= 1.0 %
<= 1.0 %
Iron, Fe 38.33 - 48.25 %
38.33 - 48.25 %
Lead, Pb <= 0.0050 %
<= 0.0050 %
Manganese, Mn <= 2.0 %
<= 2.0 %
Nickel, Ni 34 - 37 %
34 - 37 %
Phosphorous, P <= 0.030 %
<= 0.030 %
Silicon, Si 0.75 - 1.5 %
0.75 - 1.5 %
Sulfur, S <= 0.030 %
<= 0.030 %
Tin, Sn <= 0.025 %
<= 0.025 %
Electrical Properties Metric English Comments
Magnetic Permeability 1.02
1.02
B-H at 200H