Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Modulus of Elasticity | 15.0 - 18.0 GPa | 2180 - 2610 ksi | Injection and Compression; ISO 527 |
Raschig Group 3505 Epoxy Glass-fiber reinforced epoxy molding compound. Good mechanical strength, very good electrical isolation properties and dimensional stability even at high temperatures. This product meets the allowed.. |
|||
Modulus of Elasticity | 15.0 - 18.0 GPa | 2180 - 2610 ksi | Injection and Compression; ISO 527 |
Raschig Group 3535 Epoxy Glass fiber-reinforced epoxy molding compound. Good mechanical strength, very good electrical isolation properties adn dimensional stability even at high temperatures. Form: Low dust granulate pack.. |
|||
Modulus of Elasticity | 15.0 - 18.0 GPa | 2180 - 2610 ksi | Injection and Compression; ISO 527 |
Raschig Group 3536 Epoxy Glass-fiber reinforced epoxy molding compound. Good mechanical strength, very good electrical isolation properties and dimensional stability even at high temperatures. This product meets the allowed.. |
|||
Modulus of Elasticity | 15.0 - 18.0 GPa | 2180 - 2610 ksi | Injection and Compression; ISO 527 |
Raschig Group EPOXIDUR® 3581 T-1 EP Epoxy, Molded, Glass Fiber Filler Glass-fiber reinforced and inorganically filled epoxy molding compound. Good mechanical strength, very good electrical isolation properties and dimensional stability even at high temperatures. Very .. |
|||
Modulus of Elasticity | 15.0 - 18.0 GPa | 2180 - 2610 ksi | Injection and Compression; ISO 527 |
Raschig Group EPOXIDUR® 3582 EP Epoxy Glass-fiber reinforced and inorganically filled epoxy molding compound. Good mechanical strength, very good electrical isolation properties and dimensional stability even at high temperatures. Moldi.. |
|||
Modulus of Elasticity | 15.0 - 18.0 GPa | 2180 - 2610 ksi | Injection and Compression; ISO 527 |
Raschig Group EPOXIDUR® 3585 EP Epoxy, Molded, Glass Fiber Filler Glass-fiber reinforced and inorganically filled epoxy molding compound. Good mechanical strength, very good electrical isolation properties and dimensional stability even at high temperatures, excel.. |
|||
Modulus of Elasticity | 14.0 - 18.0 GPa | 2030 - 2610 ksi | Compression; ISO 527 |
Raschig Group RESINOL® 87120 EPF Phenolic Glass-fiber reinforced phenolic molding compound. Excellent heat resistance, low mould shrinkage and post-shrinkage, good chemical resistance and very good mechanical properties. This product meets .. |
|||
Modulus of Elasticity | 5.86 - 18.0 GPa | 850 - 2610 ksi | Average value: 11.7 GPa Grade Count:17 |
Overview of materials for Nylon 46, Flame Retarded + Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 46, Flame Retarded + Glass Fiber Reinforced". Each property range of values reported is minimum an.. |