Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Modulus of Elasticity | 0.000800 GPa | 0.116 ksi | 10% Modulus, Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
DuPont Performance Polymers VTR 8550 (GFLT-S) Peroxide Cured Fluoroelastomer (FKM) Formulation
(discontinued FormulationVTR-8550 |
|||
Modulus of Elasticity | 0.000800 GPa | 0.116 ksi | 10% Modulus, Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
DuPont Performance Polymers VTR 8505/8500 Formulation
(discontinued **) FormulationViton® 8505 |
|||
Modulus of Elasticity | 0.000800 GPa | 0.116 ksi | 10% Modulus, Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
DuPont Performance Polymers VTR 8655 (GBL-S) , VTR 8650 8655/8650 Blend
(discontinued **) FormulationVTR 8655 |