Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Compressive Strength | 320 MPa | 46400 psi | ISO 604 |
Schwartz Technical Plastics MITELA® 2/5 A Cotton Fabric, Special Quality Application: bearing shells and bearing collarsInformation provided by Schwartz Technical Plastics GmbH |
|||
Compressive Strength | 320 MPa | 46400 psi | ISO 604 |
Schwartz Technical Plastics MITELA® HD8B Cotton Fabric, Special Quality Application: bearing shells and bearing collarsInformation provided by Schwartz Technical Plastics GmbH |
|||
Compressive Strength | 320 MPa | 46400 psi | ISO 604 |
Sumitomo Bakelite North America CF 9040A Carbon Fiber Reinforced Phenolic CF 9040A is a high strength carbon fiber phenolic molding compoundInformation provided by Sumitomo Bak North America, Inc. |
|||
Compressive Strength | 320 MPa @Thickness >=5.00 mm |
46400 psi @Thickness >=0.197 in |
24hr/23°C/50% RH; ISO 604; IEC/EN 60893-2 5.3 |
Elektro-Isola Etronax MF Phenolic, Cotton Fabric Reinforcement, Brown, Sheets Description: Exclusively for mechanical applications. Impact-resistant, resistant to mechanical wear, noise-reducing, low friction. Well suited for parts where there are high mechanical load and wea.. |
|||
Compressive Strength | 320 MPa @Thickness >=5.00 mm |
46400 psi @Thickness >=0.197 in |
24hr/23°C/50% RH; ISO 604; IEC/EN 60893-2 5.3 |
Elektro-Isola Etronax MFP G Phenolic, Cotton/synthetic Fabric Reinforcement, Black, Sheets Description: Exclusively for mechanical applications. The combination of cotton/synthetic reinforcement and a graphite-modified resin results in a material with low friction and especially high wear.. |
|||
Compressive Strength | 320 MPa @Thickness >=5.00 mm |
46400 psi @Thickness >=0.197 in |
24hr/23°C/50% RH; ISO 604; IEC/EN 60893-2 5.3 |
Elektro-Isola Etronit AS Phenolic, Paper Reinforcement, Black, Sheets Description: ESD-protection quality according to SP-method 2472, IEC 61340-5-1 and EN 100015-1. SP ESD Approval Certificate No. 230-01-0137. High mechanical properties at temperatures up to 120°CAp.. |
|||
Compressive Strength | 320 MPa @Thickness >=5.00 mm |
46400 psi @Thickness >=0.197 in |
24hr/23°C/50% RH; ISO 604; IEC/EN 60893-2 5.3 |
Elektro-Isola Etronit IIQ Phenolic, Paper Reinforcement, Dark Brown, Sheets Description: Mechanically a good Etronit type with electrical properties adequate for insulation in low-voltage applications. Applications: Used in electrical appliances, bus-bar carriers, partition.. |
|||
Compressive Strength | 320 MPa @Thickness >=5.00 mm |
46400 psi @Thickness >=0.197 in |
24hr/23°C/50% RH; ISO 604; IEC/EN 60893-2 5.3 |
Elektro-Isola Etronit IIQ S AL Phenolic, Paper Reinforcement, Black with foil, Sheets Description: Mechanically a good Etronit type with electrical properties adequate for insulation in low-voltage applications. Material is black throughout. Elegant surface finish combined with good .. |
|||
Compressive Strength | 320 MPa @Thickness >=5.00 mm |
46400 psi @Thickness >=0.197 in |
24hr/23°C/50% RH; ISO 604; IEC/EN 60893-2 5.3 |
Elektro-Isola Etronit IIQ S Phenolic, Paper Reinforcement, Black, Sheets Description: Mechanically a good Etronit type with electrical properties adequate for insulation in low-voltage applications. Material is black throughout. Elegant surface finish combined with good .. |
|||
Compressive Strength | 320 MPa @Treatment Temp. 100 °C, Time 3600 sec |
46400 psi @Treatment Temp. 212 °F, Time 1.00 hour |
ISO 604; IEC/EN 60893-2 5.3 |
Elektro-Isola G-Etronax PM H Polyester, Glass Mat, Creme, Sheets Description: A reasonably-priced alternative to other high-temperature types. Low thermal conductivity. Applications: Used as, among other things, thermal insulation plates where high strength prope.. |