Polymer Property : Compressive Strength = 250 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Compressive Strength	250 MPa	36300 psi
Pyrotek TS-114 Thermoset Electrical Insulation Product (Nema Grade: GPO-3) Glass reinforcement, Polyester resin, Red color. Flame retardant. Excellent arc and track resistance. UL recognized.Information provided by Pyrotek.
Compressive Strength	250 MPa	36300 psi
Pyrotek TS-117 Thermoset Electrical Insulation Product (Nema Grade: GPO-1) Glass reinforcement, Polyester resin, Gray color. Economical, general purpose product.Information provided by Pyrotek.
Compressive Strength	250 MPa	36300 psi	Test specimen flat tested; ISO 604
Hexion Bakelite™ PF 31 Phenolic Formaldehyde Resin, UL Listed (discontinued **) Phenolic molding compound, mainly organically filled, standard molding compound for normal stress, UL listed molding compound 1.5 mm/V-1 (All), 3 mm/V-0 (All), standardized molding compound.Applicat..
Compressive Strength	250 MPa	36300 psi	Test specimen flat tested; ISO 604
Hexion Bakelite™ PF 2137 Phenolic Formaldehyde Resin, High Surface Quality, Dishwasher Proof (discontinued ** Phenolic molding compound, inorganically/organically filled, glass fiber reinforced, increased heat resistance, minimal distortion, dish washer proof.Application areas: Iron heat shields, fittings f..
Compressive Strength	250 MPa	36300 psi	Test specimen flat tested; ISO 604
Hexion Bakelite™ PF 2400 Phenolic Formaldehyde Resin, High Surface Quality, Dishwasher Proof, UL Listed (disc Phenolic molding compound, inorganically/organically filled, average heat resistance, increased dimensional stability, dish washer proof, UL listed molding compound 1.5 mm/V-0 (ALL).Application area..
Compressive Strength	250 MPa	36300 psi	Test specimen flat tested; ISO 604
Hexion Bakelite™ PF 6506 Phenolic Formaldehyde Resin, Low Shrinkage, Resistant to High Temperatures, UL Listed &nbs Phenolic molding compound, inorganically filled, glass fiber reinforced, high dimensional stability at raised temperature, good media resistance, heat-resistant, UL listed molding compound 1.5 mm/V-..
Compressive Strength	250 MPa	36300 psi	Test specimen flat tested; ISO 604
Hexion Bakelite™ PF 7400 Phenolic Formaldehyde Resin, High Mechanical Strength (discontinued **) Phenolic molding compound, organically filled, reinforced with cotton fiber flakes, high notched impact strength.Application areas: Moldings for higher mechanical strain, e.g. power plugs high volta..
Compressive Strength	250 MPa	36300 psi	Test specimen flat tested; ISO 604
Hexion Bakelite™ X24 Phenolic Formaldehyde Resin (discontinued **) Phenolic molding compound, mainly organically filled.Application areas: Operating controls, housing parts, lamp holders.Information provided by Bak AGBak AG became a part of Hexion in 2005.
Compressive Strength	250 MPa	36300 psi	ASTM D695
Sumitomo Bakelite North America E 3938A Hardware Grade Epoxy Fiberglass reinforced epoxy molding compound with excellent dimensional stability, good strength and excellent electrical insulation properties.Information provided by Vyncolit, a Sumitomo Bak Group..
Compressive Strength	250 MPa @Temperature 23.0 °C, Time 86400 sec	36300 psi @Temperature 73.4 °F, Time 24.0 hour	50% RH, Axial; ISO 604; IEC/EN 61212-2 5.2
Elektro-Isola G-Etronax EP 11 Epoxy, Glass Fabric Reinforcement, Green, Tubes Description: Particularly good electrical and mechanical properties. Extremely high mechanical strength, even at high temperatures. Retains electrical properties at high air humidity. High resistanc..
Compressive Strength	250 MPa @Treatment Temp. 100 °C, Time 3600 sec	36300 psi @Treatment Temp. 212 °F, Time 1.00 hour	ISO 604; IEC/EN 60893-2 5.3
Elektro-Isola G-Etronax PM 953 Polyester, Glass Mat, Off White, Sheets Description: Good electrical properties such as high breakdown voltage in air and oil and highest arc resistance and tracking resistance. Self-extinguishing. Low smoke emission, halogen-free. Very m..
Compressive Strength	>= 250 MPa	>= 36300 psi	Perpendicular to laminations; IEC 1212-2 5.3
Hippe PF CP 203 Cellulose Paper Reinforced Phenolic Resin - Sheet Used in mechanical and electrical applications. Good electrical properties under normal humidity. Also available in hot-punching versions.Information provided by Hippe.
Compressive Strength	>= 250 MPa	>= 36300 psi	Perpendicular to laminations; IEC 1212-2 5.3
Hippe PF CP 204 Cellulose Paper Reinforced Phenolic Resin - Sheet Used in electrical and electronic applications. Good stability of electrical properties under high humidity. Also available in cold or hot-punching versions.Information provided by Hippe.
Compressive Strength	>= 250 MPa	>= 36300 psi	Perpendicular to laminations; IEC 1212-2 5.3
Hippe PF CP 205 Cellulose Paper Reinforced Phenolic Resin - Sheet Used in electrical and electronic applications. Good stability of electrical properties under high humidity. Also available in cold or hot-punching versions. Flame retardant.Information provided ..
Compressive Strength	>= 250 MPa	>= 36300 psi	Perpendicular to laminations; IEC 1212-2 5.3
Hippe PF CP 206 Cellulose Paper Reinforced Phenolic Resin - Sheet Used in mechanical and electrical applications. Good electrical properties under normal humidity. Also available in hot-punching versions.Information provided by Hippe.
Compressive Strength	>= 250 MPa	>= 36300 psi	Perpendicular to laminations; IEC 1212-2 5.3
Hippe UP GM 204 Woven Glass Mat Reinforced Polyester (unsaturated) Resin - Sheet Used in mechanical and electrical applications. Very high mechanical properties at ambient temperatures. Good mechanical properties at elevated temperatures.Information provided by Hippe.
Compressive Strength	>= 250 MPa	>= 36300 psi	Perpendicular to laminations; IEC 1212-2 5.3
Hippe UP GM 205 Woven Glass Mat Reinforced Polyester (unsaturated) Resin - Sheet Used in mechanical and electrical applications. Very high mechanical properties at ambient temperatures. Good mechanical properties at elevated temperatures. Flame retardant.Information provided ..
Compressive Strength	250 MPa	36300 psi	ISO 604
Vyncolit X611 Novolac Phenolic Glass fiber filled phenolic molding compound with excellent mechanical and thermal properties. UL listed.USES: Complex precision parts with thin cross section and good mechanical properties e.g. in..
Compressive Strength	250 - 300 MPa	36300 - 43500 psi	ISO 604
Raschig Group DECAL® 152CL Phenolic Glass-fiber and mineral reinforced phenolic molding compound. Excellent heat resistance, low mould shrinkage and post-shrinkage, good chemical resistance and mechanical properties. This product meet..
Compressive Strength	250 - 300 MPa	36300 - 43500 psi	ISO 604
Raschig Group RESINOL® 400 EPF Phenolic Glass-fiber reinforced phenolic molding compound. Excellent heat resistance, low mould shrinkage and post-shrinkage, good chemical resistance and very good mechanical properties. This product meets ..
Compressive Strength	250 MPa	36300 psi	Test specimen flat tested; ISO 604
Hexion Bakelite™ PF 4260 Phenolic Formaldehyde Resin, Resistant to High Temperatures, Improved Electrical Properties, Low Shrinkage, High Mechanical Strength Phenolic molding compound, inorganically filled, glass fiber reinforced, high dimensional stability at raised temperature, good media resistance, heat-resistantApplication areas: Commutators (starte..