Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Compressive Strength | 1.10 MPa | 160 psi | to 30% deformation |
Pyrotek MT-29P Microporous Panel Insulation MT-29P is a unique panel insulation which offers exceptionally low thermal conductivity. The exterior of the panel is a glass fabric which maximizes the strength of the rigid interior panel.Applica.. |
|||
Compressive Strength | 1.10 MPa | 160 psi | to 30% deformation |
Pyrotek MT-29Q Quilted Microporous Insulation MT-29Q is quilted to encapsulate its microporous core between glass cloth. The result is a flexible insulating material which offers exceptionally low thermal conductivity. The quilting maintains .. |
|||
Compressive Strength | 1.10 MPa | 160 psi | to 30% deformation |
Pyrotek MT-29L Microporous Ladle Lining Insulation MT-29L is a microporous insulation material covered with a flexible glass fabric. Parallel-stitched for ease of handling during installation, it is designed for use between ladle shells and the bac.. |
|||
Compressive Strength | >= 1.10 MPa | >= 160 psi | @ 20 kg/m<sup>2</sup>; JIS A9511, ASTM D1621 |
Samsung Cheil Industries Starex® SG-301 Expandable Polystyrene (EPS) High Expansion Typical Application : Large FloatInformation provided by Samsung Cheil Industries. |
|||
Compressive Strength | >= 1.10 MPa | >= 160 psi | @ 20 kg/m<sup>2</sup>; JIS A9511, ASTM D1621 |
Samsung Cheil Industries Starex® SG-302 Expandable Polystyrene (EPS) High Expansion Typical Application : Large Float, Fish Box (Large)Information provided by Samsung Cheil Industries. |
|||
Compressive Strength | >= 1.10 MPa | >= 160 psi | @ 20 kg/m<sup>2</sup>; JIS A9511, ASTM D1621 |
Samsung Cheil Industries Starex® SG-301 Expandable Polystyrene (EPS) High Expansion Typical Application : Large FloatInformation provided by Samsung Cheil Industries. |
|||
Compressive Strength | >= 1.10 MPa | >= 160 psi | @ 20 kg/m<sup>2</sup>; JIS A9511, ASTM D1621 |
Samsung Cheil Industries Starex® SG-302 Expandable Polystyrene (EPS) High Expansion Typical Application : Large Float, Fish Box (Large)Information provided by Samsung Cheil Industries. |
|||
Compressive Strength | 1.10 MPa | 160 psi | Cold Crushing Strength |
Zircar Ceramics MICROSIL Microporous Insulation MICROSIL Microporous Insulation is an insulation material. Having thermal conductivity an order of magnitude lower than ceramic fiber materials Microsil Microporous Insulation can be an integral par.. |
|||
Compressive Strength | 1.10 MPa | 160 psi | Lower Yield in the Through Plane Direction |
Cymat A35620SC 030SS Stabilized Aluminum Foam Description: Cymat A35620SC 030SS stabilized aluminum foam (SAF) is a closed cell aluminum foam formed from A356 aluminum alloy with a density of 0.3 g/cm3. The mechanical properties of SAF make it .. |
|||
Compressive Strength | 1.10 MPa | 160 psi | average; perpendicular to plane; ISO 844 |
3A Composites Core Materials AIREX® R82.80 High Performance Structural Foam AIREX® R82 is a closed-cell, thermoplastic polymer foam that combines fire resistance with low smoke and toxicity, along with good dielectric properties. It has a good strength to weight ratio, ver.. |
|||
Compressive Strength | 1.10 MPa | 160 psi | |
BNZ Materials 2337LI Insulating Aggregate BNZ manufactures a variety of insulating and dense castable refractories to meet the exacting needs of the high temperature processing industries. These hydraulic setting products are suitable for i.. |
|||
Compressive Strength | 1.10 MPa | 160 psi | to 30% deformation with density of 0.288 g/cc |
Pyrotek MT-29B Microporous Insulating Board MT-29B has the low thermal conductivity. Its cellular structure contributes to its low-weight, good compressive strength, and low shrinkage at high temperatures.ApplicationsBackup insulation for: T.. |
|||
Compressive Strength | >= 1.10 MPa | >= 160 psi | perpendicular to plane; ISO 844 |
3A Composites Core Materials AIREX® C70.75 Universal Structural Foam AIREX® C70 is a closed cell, crosslinked polymer foam that combines excellent stiffness and strength to weight ratios with superior toughness. It is non-friable, contains no CFC’s, has negligible .. |