Polymer Property : Compressive Strength = 145 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Compressive Strength	>= 1.00 MPa	>= 145 psi	@ 20 kg/m<sup>2</sup>; JIS A9511, ASTM D1621
Samsung Cheil Industries StarexÂ® SG-401 Expandable Polystyrene (EPS) High Expansion Typical Application : Large FloatInformation provided by Samsung Cheil Industries.
Compressive Strength	>= 1.00 MPa	>= 145 psi	@ 20 kg/m<sup>2</sup>; JIS A9511, ASTM D1621
Samsung Cheil Industries StarexÂ® SG-401 Expandable Polystyrene (EPS) High Expansion Typical Application : Large FloatInformation provided by Samsung Cheil Industries.
Compressive Strength	1.00 MPa @Time 3.60e+7 sec	145 psi @Time 10000 hour
Wolf Kunststoff ZEDEX® ZX-550 A5L Polymer Alloy Main Characteristics: Strong anti-adhesive; Low creep; Weather resistant; No water absorption; Good machinability; Strongly viscoelastic; Stress resistantApplications: Chemical Engineering; Laborato..
Compressive Strength	1.00 MPa	145 psi	Upper Yield in the Through Plane Direction
Cymat A35620SC 020SS Stabilized Aluminum Foam Description: Cymat A35620SC 020SS stabilized aluminum foam (SAF) is a closed cell aluminum foam formed from A356 aluminum alloy with a density of 0.2 g/cm3. The mechanical properties of SAF make it ..
Compressive Strength	1.00 MPa	145 psi	Cold Crush Strength; ASTM C133
BNZ Materials BNZ-23A Insulating Firebrick BNZ produces many types of Insulating Fire Brick (IFB) for use in applications from 2,000°F (1,093°C) to 3,200°F (1,760°C). Each type is formulated to meet specific thermal and physical requirem..
Compressive Strength	1.00 MPa	145 psi	EN ISO 604
Brandenburger BRA-FLEX Side Insulation Information provided by Brandenburger Isoliertechnik GmbH&Co.
Compressive Strength	1.00 MPa @Temperature 200 °C	145 psi @Temperature 392 °F	EN ISO 604
Brandenburger BRA-FLEX Side Insulation Information provided by Brandenburger Isoliertechnik GmbH&Co.
Compressive Strength	1.00 MPa	145 psi	average; perpendicular to plane; ISO 844
3A Composites Core Materials AIREX® T92.80 Easy Processing Structural Foam AIREX® T92 is a closed-cell, thermoplastic and recyclable polymer foam with good mechanical properties and price / performance ratio. It has a good resistance to fatigue, is chemically stable, UV r..