Polymer Property : Tensile Strength = 95000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength	655 - 793 MPa	95000 - 115000 psi	Annealed Bar
Schmolz + Bickenbach LeanDupâ„¢ 35N Stainless Steel Bar Description: LeanDupâ„¢ 35N also known as (Uranus 35 N) is a dual phase austentic-ferritic stainless steel that has the ability to become as important as 316L. It offers better corrosion resistan..
Tensile Strength	655 - 827 MPa	95000 - 120000 psi	Escomatic Coils
Schmolz + Bickenbach UGIMAÂ® 303 HD Stainless Steel Bar Description: 303 UGIMA HDâ„¢ is a low sulfur version of Ugitechâ€™s improved machining 303 grade. It is designed to provide better metallurgical performance with respect to weldability, corros..
Tensile Strength	655 - 827 MPa @Thickness <=25.4 mm	95000 - 120000 psi @Thickness <=1.00 in	Cold Drawn Bars
Schmolz + Bickenbach UGIMAÂ® 303 HD Stainless Steel Bar Description: 303 UGIMA HDâ„¢ is a low sulfur version of Ugitechâ€™s improved machining 303 grade. It is designed to provide better metallurgical performance with respect to weldability, corros..
Tensile Strength	655 - 827 MPa	95000 - 120000 psi	Escomatic Coils
Schmolz + Bickenbach UGIMAÂ® 303 Stainless Steel Bar Description: 303 UGIMAÂ® is Ugitechâ€™s improved machining grade produced only by Ugitech. It is identical in every way to regular 303, except with respect to machinability. 303 UGIMAÂ® repre..
Tensile Strength	655 - 827 MPa @Thickness <=25.4 mm	95000 - 120000 psi @Thickness <=1.00 in	Cold Drawn Bars
Schmolz + Bickenbach UGIMAÂ® 303 Stainless Steel Bar Description: 303 UGIMAÂ® is Ugitechâ€™s improved machining grade produced only by Ugitech. It is identical in every way to regular 303, except with respect to machinability. 303 UGIMAÂ® repre..
Tensile Strength	>= 655 MPa	>= 95000 psi
Wingate Alloys Winco NT 24 Nitrogen-Strengthened Austenitic Stainless Steel Winco NT 24 provides good aqueous corrosion resistance combined with resistance to abrasives, metal-to-metal wear and sustained heats of 1500°F. Higher mechanical properties than standard austeniti..