Polymer Property : Tensile Strength = 125000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength	>= 862 MPa	>= 125000 psi
Eagle Brass 301 Austenitic Stainless Steel, 1/4 Hardened Type 301 is a chromium-nickel stainless steel that provides high strength and good ductility with chromium and nickel contents lowered to increase the work hardening range. This permits higher tens..
Tensile Strength	>= 862 MPa	>= 125000 psi
Eagle Brass 302 Austenitic Stainless Steel, 1/4 Hardened Types 302 is a widely used variation of the basic 18-8 grade with variations of nickel, chromium and carbon content. It is weakly magnetic when cold rolled.Information provided by Eagle Brass Compa..
Tensile Strength	>= 862 MPa	>= 125000 psi
Eagle Brass 305 Austenitic Stainless Steel, 1/4 Hardened Type 305 is a chromium nickel stainless steel that can be spun and deep drawn more easily due to an increased nickel content that decreases work hardening. It is nonmagnetic under most conditions. ..
Tensile Strength	>= 862 MPa	>= 125000 psi
Eagle Brass 316 Austenitic Stainless Steel, 1/4 Hardened The Mo addition increases general corrosion resistance to pitting from chloride ion solutions, and provides increased strength at elevated temperatures. Properties are similar to those of Type 304 ..
Tensile Strength	>= 862 MPa	>= 125000 psi
Eagle Brass 316L Austenitic Stainless Steel, 1/4 Hardened Type 316L is an extra-low carbon version of Type 316 that minimizes carbide precipitation. Typical uses include exhaust manifolds, furnace parts, heat exchangers, jet engine parts, pharmaceutical a..
Tensile Strength	862 MPa	125000 psi
Chicago Extruded Metals BioBrass® UNS C95520 As-Cast Aluminum Bronze This alloy is registered with the U.S. EPA as Antimicrobial.Information provided by Chicago Extruded Metals
Tensile Strength	>= 862 MPa	>= 125000 psi
Eagle Brass 304 Austenitic Stainless Steel, 1/4 Hardened Types 304 is a widely used variation of the basic 18-8 grade with variations of nickel, chromium and carbon content. It is weakly magnetic when cold rolled.Information provided by Eagle Brass Compa..
Tensile Strength	>= 862 MPa	>= 125000 psi
Eagle Brass 304L Austenitic Stainless Steel, 1/4 Hardened Type 304L is a very common variation of the basic 18-8 grade with variations of nickel, chromium and carbon content. It is weakly magnetic when cold rolled. Lower carbon 304L minimizes chromium ca..
Tensile Strength	862 MPa @Temperature -5.56 °C	125000 psi @Temperature 22.0 °F	Heat Treated to 24-32 HRC
Schmolz + Bickenbach Holder Block Plastic Mold Steel Description: Holder Block is a modified AISI-4130 material with higher chromium and molybdenum content specifically designed holder steel for molds and dies and The material is forged on a 5000 ton..