Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength | 689 - 896 MPa | 100000 - 130000 psi | |
IBC Advanced Alloys C17510 Beryllium Copper Alloy Plate, Temper AT(TF00) C17510 - Beryllium Copper mold alloys have hardnesses comparable to tool steel, but with superior thermal conductivity. Beryllium copper plate, block, bar and rounds -- upset forged and heat treated.. |
|||
Tensile Strength | 689 - 896 MPa | 100000 - 130000 psi | |
IBC Advanced Alloys C17510 Beryllium Copper Alloy Rounds, Temper AT(TF00) C17510 - Beryllium Copper mold alloys have hardnesses comparable to tool steel, but with superior thermal conductivity. Beryllium copper plate, block, bar and rounds -- upset forged and heat treated.. |
|||
Tensile Strength | >= 689 MPa @Diameter 3.17 - 88.9 mm |
>= 100000 psi @Diameter 0.125 - 3.50 in |
mid-radius; ASTM E-8 |
H.C. Starck Molybdenum Hafnium Carbide Powder, Metallurgy Alloy Bar MHC Description of Product: This specification covers molybdenum alloy (molybdenum + 1.2% hafnium) wrought bar produced from pressed and sintered metallurgy billet.Structure: The MHC alloy bars can be.. |
|||
Tensile Strength | 690 MPa | 100000 psi | |
H.C. Starck HPM 1751 Tungsten High Density Composite Description of Product: Tungsten based composite materials are outstanding due to high density and good mechanical properties. The product can be delivered both as semi-finished product for furthe.. |
|||
Tensile Strength | >= 689 MPa | >= 100000 psi | |
Eagle Brass 301 Austenitic Stainless Steel, 1/8 Hardened Type 301 is a chromium-nickel stainless steel that provides high strength and good ductility with chromium and nickel contents lowered to increase the work hardening range. This permits higher tens.. |
|||
Tensile Strength | >= 689 MPa | >= 100000 psi | |
Eagle Brass 302 Austenitic Stainless Steel, 1/8 Hardened Types 302 is a widely used variation of the basic 18-8 grade with variations of nickel, chromium and carbon content. It is weakly magnetic when cold rolled.Information provided by Eagle Brass Compa.. |
|||
Tensile Strength | >= 689 MPa | >= 100000 psi | |
Eagle Brass 316 Austenitic Stainless Steel, 1/8 Hardened The Mo addition increases general corrosion resistance to pitting from chloride ion solutions, and provides increased strength at elevated temperatures. Properties are similar to those of Type 304 .. |
|||
Tensile Strength | >= 689 MPa | >= 100000 psi | |
Eagle Brass 316L Austenitic Stainless Steel, 1/8 Hardened Type 316L is an extra-low carbon version of Type 316 that minimizes carbide precipitation. Typical uses include exhaust manifolds, furnace parts, heat exchangers, jet engine parts, pharmaceutical a.. |
|||
Tensile Strength | 689 MPa | 100000 psi | |
Chicago Extruded Metals BioBrass® UNS C62500 Aluminum Bronze Finished product available in rods.Chicago Extruded Metal temper code: M30This alloy is registered with the U.S. EPA as Antimicrobial.Information provided by Chicago Extruded Metals |
|||
Tensile Strength | >= 689 MPa | >= 100000 psi | |
Eagle Brass 304 Austenitic Stainless Steel, 1/8 Hardened Types 304 is a widely used variation of the basic 18-8 grade with variations of nickel, chromium and carbon content. It is weakly magnetic when cold rolled.Information provided by Eagle Brass Compa.. |
|||
Tensile Strength | >= 689 MPa | >= 100000 psi | |
Eagle Brass 304L Austenitic Stainless Steel, 1/8 Hardened Type 304L is a very common variation of the basic 18-8 grade with variations of nickel, chromium and carbon content. It is weakly magnetic when cold rolled. Lower carbon 304L minimizes chromium ca.. |