Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 6.5 - 16 g/10 min @Load 21.6 kg, Temperature 190 °C |
6.5 - 16 g/10 min @Load 47.6 lb, Temperature 374 °F |
|
Kazanorgsintez PE80B-275 Medium Density Polyethylene Composite Production Method: Copolymerization of ethylene at low pressure using advanced technology and in presence of complex catalysts on carrier material that allows production of polyethylene with enhanc.. |
|||
Melt Flow | 6.5 - 16 g/10 min @Load 21.6 kg, Temperature 190 °C |
6.5 - 16 g/10 min @Load 47.6 lb, Temperature 374 °F |
|
Kazanorgsintez PE80B-286 Medium Density Polyethylene Composite Production Method: Copolymerization of ethylene at low pressure using advanced technology and in presence of complex catalysts on carrier material that allows production of polyethylene with enhanc.. |
|||
Melt Flow | 6.5 g/10 min @Load 10.0 kg, Temperature 220 °C |
6.5 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM-D1238 |
Ineos ABS Lustran® 720 ABS, Molding Grade Lustran® ABS 720 resin is a black, virgin injection molding grade of ABS (acrylonitrile butadiene styrene). It is supplied as salt-and-pepper pellets with color concentrate 901802 black. Designed.. |
|||
Melt Flow | 6.5 g/10 min @Load 2.16 kg, Temperature 250 °C |
6.5 g/10 min @Load 4.76 lb, Temperature 482 °F |
Part; ISO 1133 |
DuPont Performance Polymers Crastin® CE2056 NC010 PBT Crastin® CE2056 NC010 is an unreinforced polybutylene terephthalate molding resin.Information provided by DuPont Performance Polymers |
|||
Melt Flow | 6.5 g/10 min @Load 3.80 kg, Temperature 230 °C |
6.5 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
Chi Mei Kibisan® PN-127 SAN Heat Resistant |
|||
Melt Flow | 6.5 g/10 min @Load 3.80 kg, Temperature 230 °C |
6.5 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
Chi Mei Kibisan® PN-127H SAN Chemical Resistant |
|||
Melt Flow | 6.5 g/10 min @Load 1.20 kg, Temperature 300 °C |
6.5 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D 1238 |
SABIC Innovative Plastics Lexan® EXL1033C PC Copolymer Lexan*EXL1033C polycarbonate (PC) siloxane copolymer resin is a low flow, UV stabilized grade designed for (co)-extrusion. This resin offers low temperature (-30C) ductility and excellent extrusion .. |