Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 7.7 g/10 min | 7.7 g/10 min | ASTM D1238 |
LyondellBasell Alathon® M6580 High Density Polyethylene ApplicationsALATHON M 6580 is a narrow molecular weight distribution homopolymer that enhances processability and stiffness, exhibits excellent color, low odor and good processing stability. Typica.. |
|||
Melt Flow | 7.7 g/10 min @Load 5.00 kg, Temperature 280 °C |
7.7 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D1238 |
SABIC Innovative Plastics NORYL REN501 PPE+PS Noryl REN501 resin is an unfilled Post Industrial Recycle (PIR) based injection moldable modified polyphenylene ether blend comprising up to 40% PIR content. Available in black only. |
|||
Melt Flow | 7.7 g/10 min @Load 2.16 kg, Temperature 235 °C |
7.7 g/10 min @Load 4.76 lb, Temperature 455 °F |
ASTM D1238R |
UBE UBESTA® 3030JLX1 Plasticized Automotive Grade Nylon 12 Description: UBE UBESTA® Automotive grade Nylon 12Comments: UV resistance, heat resistanceInformation provided by UBE. |
|||
Melt Flow | 7.7 g/10 min @Load 2.16 kg, Temperature 190 °C |
7.7 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238, ISO 1133 |
DuPont™ Bynel® 21E533 Anhydride Modified Ethylene Acrylate BYNEL® Series 2100 resins are anhydride modified ethylene acrylate resins. They contain a temperature stable ester which makes them functional in high temperature coextrusions. They are available i.. |
|||
Melt Flow | 7.7 g/10 min @Load 2.16 kg |
7.7 g/10 min @Load 4.76 lb |
|
Dow Primacor® 4608 Ethylene Acrylic Acid (EAA) PRIMACOR® 4608 polymer containing 6.5% comonomer is an extrusion/ coextrusion coating and laminating resin. It is designed to provide excellent adhesion to metallic, paper and polyethylene substrat.. |
|||
Melt Flow | 7.7 g/10 min | 7.7 g/10 min | ASTM D1238 |
Asahi Kasei Thermofil P6-30FM-0801 30% Fiber Mineral Filled, Heat Stabilized Information provided by Asahi Thermofil |