Polymer Property : Melt Flow = 19.2 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Physical Properties Metric English Comments
Melt Flow 19.2 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 19.2 g/10 min

@Load 4.76 lb,
Temperature 374 °F
Lehmann & Voss LUVOCOM® 80-7695 Polyacetal-copolymer, with glass fiber and PTFE
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Emergency running property, gl..
Melt Flow 19.2 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 19.2 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 Calculated from Volume Flow Rate of 16 cm<sup>3</sup>/10min.; ISO 1133
Mitsubishi Xantar® 19 R Polycarbonate
Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances ..
Melt Flow 19.2 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 19.2 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 Calculated from Volume Flow Rate of 16 cm<sup>3</sup>/10min.; ISO 1133
Mitsubishi Xantar® 19 SR FD Polycarbonate
Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances ..
Melt Flow 19.2 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 19.2 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 Calculated from Volume Flow Rate of 16 cm<sup>3</sup>/10min.; ISO 1133
Mitsubishi Xantar® 19 UR Polycarbonate
Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances ..
Melt Flow 19.2 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 19.2 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 Calculated from Volume Flow Rate of 16 cm<sup>3</sup>/10min.; ISO 1133
Mitsubishi Xantar® FC 19 R Polycarbonate
Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances ..
Melt Flow 19.2 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 19.2 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 Calculated from Volume Flow Rate of 16 cm<sup>3</sup>/10min.; ISO 1133
Mitsubishi Xantar® FC 19 UR Polycarbonate
Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances ..
Melt Flow 19.2 g/10 min

@Load 2.16 kg,
Temperature 230 °C
 19.2 g/10 min

@Load 4.76 lb,
Temperature 446 °F
 ASTM D1238
Multibase Multi-Flex® A 8814 Black TPE Thermoplastic Elastomer
Forms: PelletsProcessing Methods:Injection Molding Information provided by Multibase
Melt Flow 19.2 g/10 min

@Load 5.00 kg,
Temperature 300 °C
 19.2 g/10 min

@Load 11.0 lb,
Temperature 572 °F
 ASTM D1238
SABIC Innovative Plastics NORYL FM3020V PPE+PS (Asia Pacific)
30% filled FR high modulus foam grade