Polymer Property : Melt Flow = 18.2 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Melt Flow	18.2 g/10 min @Load 1.20 kg, Temperature 300 °C	18.2 g/10 min @Load 2.65 lb, Temperature 572 °F	ASTM D1238
SABIC Innovative Plastics Lexan® FXD121R PC Transparent/translucent PC for light diffusion special effects. MFR of 18.2. Color package may affect performance.
Melt Flow	18.2 g/10 min @Load 1.20 kg, Temperature 300 °C	18.2 g/10 min @Load 2.65 lb, Temperature 572 °F	ASTM D1238
SABIC Innovative Plastics Lexan® FXD121R PC (Asia Pacific) Transparent/translucent PC for light diffusion special effects. MFR of 18.2. Color package may affect performance.
Melt Flow	18.2 g/10 min @Load 1.20 kg, Temperature 300 °C	18.2 g/10 min @Load 2.65 lb, Temperature 572 °F	ASTM D1238
SABIC Innovative Plastics Lexan® FXE121R PC Transparent PC. ILLUMINATE special effects (fluorescent/edge glow colors). MFR 18.2. Internal mold release.
Melt Flow	18.2 g/10 min @Load 1.20 kg, Temperature 300 °C	18.2 g/10 min @Load 2.65 lb, Temperature 572 °F	ASTM D1238
SABIC Innovative Plastics Lexan® FXG121R PC PC in special effects colors. ""Diamond Sparkle"" appearance additives. Color package may affect performance.
Melt Flow	18.2 g/10 min @Load 1.20 kg, Temperature 300 °C	18.2 g/10 min @Load 2.65 lb, Temperature 572 °F	ASTM D1238
SABIC Innovative Plastics Lexan® FXM121R PC PC in special effects colors. Metallic and pearlescent additives. Color package may affect performance.
Melt Flow	18.2 g/10 min @Load 1.20 kg, Temperature 300 Â°C	18.2 g/10 min @Load 2.65 lb, Temperature 572 Â°F	ASTM D1238
SABIC Innovative Plastics LNP LUBRICOMP Lexan_WR2210 PC LNP* Lubricomp* Lexan_WR2210 compound is an alternative polymeric wear additive technology. No silicones, superior processability/part appearance. Flow similar to LEXAN 121.
Melt Flow	18.2 g/10 min @Load 1.20 kg, Temperature 300 Â°C	18.2 g/10 min @Load 2.65 lb, Temperature 572 Â°F	ASTM D1238
SABIC Innovative Plastics LNP LUBRICOMP Lexan_WR2210 PC (Asia Pacific) Alternative polymeric wear additive technology. No silicones, superior processability/part appearance. Flow similar to LEXAN 121.