SABIC Innovative Plastics LNP LUBRICOMP Lexan_WR2210 PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP Lexan_WR2210 PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubricomp* Lexan_WR2210 compound is an alternative polymeric wear additive technology. No silicones, superior processability/part appearance. Flow similar to LEXAN 121.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 18.2 g/10 min @Load 1.20 kg, Temperature 300 °C |
18.2 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 62.0 MPa | 8990 psi | Type I, 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 59.0 MPa | 8560 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 94 % | 94 % | Type I, 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 88.0 MPa | 12800 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.39 GPa | 347 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 6.56 J/cm | 12.3 ft-lb/in | ASTM D256 |
| Tensile Impact Strength | 630 kJ/m² | 300 ft-lb/in² | Type S; ASTM D1822 |
| Dart Drop, Total Energy | 56.0 J | 41.3 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Coefficient of Friction, Dynamic | 0.21 | 0.21 | steel; ASTM D1894 |
| Coefficient of Friction, Static | 0.17 | 0.17 | steel; ASTM D1894 |
| K (wear) Factor | 171 x 10-8 mm³/N-M | 85.0 x 10-10 in³-min/ft-lb-hr | PV=2000 psi-fpm vs Self; SABIC Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C @Thickness 3.20 mm |
261 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| 127 °C @Thickness 6.40 mm |
261 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| UL RTI, Electrical | 100 °C | 212 °F | UL 746B |
| UL RTI, Mechanical with Impact | 100 °C | 212 °F | UL 746B |
| UL RTI, Mechanical without Impact | 100 °C | 212 °F | UL 746B |
| Flammability, UL94 | HB @Thickness 1.47 mm |
HB @Thickness 0.0579 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Arc Resistance | 120 - 180 sec | 120 - 180 sec | Tungsten; ASTM D495 |
| Comparative Tracking Index | 175 - 250 V | 175 - 250 V | UL 746A |
| Hot Wire Ignition, HWI | 30 - 60 sec | 30 - 60 sec | UL 746A |
| High Amp Arc Ignition, HAI | 60 - 120 arcs | 60 - 120 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 25.4 - 80.0 mm/min | 1.00 - 3.15 in/min | UL 746A |
Users viewing this material also viewed the following:
- Polymer Resources PC-G20 Polycarbonate, 20% Glass Reinforced
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 120 PHR N990 Filler
- Solvay Specialty Polymers Diofan® A 610 Polyvinylidene Chloride (PVDC)
- Teknor Apex APEX® 3302-90 Polyvinyl Chloride, Flexible
- Zhejiang Double Fish YS-G030 30% Long Fiber Glass Reinforced Polypropylene
- ChevronTexaco 100R Neutral Oil
- ExxonMobil AXO3BE3 Polypropylene Homopolymer
- ExxonMobil Oppalyte™ 38ICE OPP Film
- ConocoPhillips Synterra™ 2 Hydraulic Oil, AGMA No. 2
Copyright © lookpolymers.com All Rights Reserved