- Polymer Property : Melt Flow = 16.5 g/10 min
Polymer Property : Melt Flow = 16.5 g/10 min Product List
Physical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 16.5 g/10 min | 16.5 g/10 min | ASTM D1238 |
| Multibase Multi-Pro® 2516 CU Polypropylene Calcium Carbonate Filler, 25% by weight.Features:Gloss, High UV Resistance, Good Forms:PelletsProcessing Methods:Injection MoldingUses:FurnitureLawn and Garden EquipmentInformation provided by Mult.. |
|||
| Melt Flow | 16.5 g/10 min | 16.5 g/10 min | ASTM D1238 |
| Multibase Multi-Pro® 4615 X White Polypropylene Forms:PelletsProcessing Methods:Injection MoldingInformation provided by Multibase |
|||
| Melt Flow | 16.5 - 19.5 g/10 min @Load 2.16 kg, Temperature 230 °C |
16.5 - 19.5 g/10 min @Load 4.76 lb, Temperature 446 °F |
Procedure A Condition L; ASTM D1238 |
| Network Polymers NPP 30-1800 Description: Homopolymer PolypropyleneInformation provided by Network Polymers Inc. |
|||
| Melt Flow | 16.5 g/10 min @Load 2.16 kg, Temperature 260 °C |
16.5 g/10 min @Load 4.76 lb, Temperature 500 °F |
ASTM D1238 |
| SABIC Innovative Plastics Cycoloy® CM6240 PC+ABS (Asia Pacific) CYCOLOY CM6240 resin is a flame retardant PC/ABS blend featuring balanced properties of high modulus, good flow and ductility. It is of Br- & Cl-free flame retardant systems intended to meet thin wa.. |
|||
| Melt Flow | 16.5 g/10 min | 16.5 g/10 min | Condition G |
| Ineos Nova 3500 General Purpose Crystal Polystyrene
(discontinued **) Good blending resin, Suitable for difficult to fill and thin wall molding, USP Class VIApplications: Cosmetic and medical packaging, Housewares, Consumer Electronic packaging, ToysExposure to gamma .. |
|||
| Melt Flow | 16.5 g/10 min | 16.5 g/10 min | Condition G |
| Ineos Nova 3504 General Purpose Crystal Polystyrene
(discontinued **) Good blending resin, Suitable for difficult to fill an thin wall molding, USP Class VIApplications: Cosmetic and medical packaging, Housewares, Consumer Electronic packaging, ToysExposure to gamma r.. |
|||
| Melt Flow | 16.5 g/10 min @Load 2.16 kg, Temperature 250 °C |
16.5 g/10 min @Load 4.76 lb, Temperature 482 °F |
|
| Lehmann & Voss LUVOCOM® 1850-7795 PBT, with PTFE Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Isotropic shrinkage characteri.. |
|||
| Melt Flow | 16.5 g/10 min @Load 1.20 kg, Temperature 300 °C |
16.5 g/10 min @Load 2.65 lb, Temperature 572 °F |
|
| Mitsubishi Iupilon® S3000R 16.5 MFI Polycarbonate With Release Information provided by US distributor Polymer Technology and Services, LLC (PTS). |
|||
| Melt Flow | 16.5 g/10 min @Load 1.20 kg, Temperature 300 °C |
16.5 g/10 min @Load 2.65 lb, Temperature 572 °F |
|
| Mitsubishi Iupilon® S3000UR 16.5 MFI, UV Stabilized Polycarbonate With Release Information provided by US distributor Polymer Technology and Services, LLC (PTS). |
|||
| Melt Flow | 16.5 g/10 min @Load 1.20 kg, Temperature 300 °C |
16.5 g/10 min @Load 2.65 lb, Temperature 572 °F |
|
| Mitsubishi Iupilon® S3001R 16.5 MFI FDA Compliant Polycarbonate With Release Information provided by US distributor Polymer Technology and Services, LLC (PTS). |
|||
| Melt Flow | 16.5 g/10 min @Load 2.16 kg, Temperature 230 °C |
16.5 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Styron INSPIREâ„¢ TF0808S(U) Polypropylene TF0808S(U) is a talc filled PP exhibiting high impact resistance and a high stiffness. It is particularly well suited for low wall thickness bumper skins. INSPIRE TF0808S for painted parts INSPIRE .. |
|||
| Melt Flow | 16.5 g/10 min @Load 2.16 kg, Temperature 250 °C |
16.5 g/10 min @Load 4.76 lb, Temperature 482 °F |
ISO 1133 |
| Polyram RamSter RF303G6 PBT, 30% Glass Fiber, Industrial Grade Industrial Grade, 30% glass fiber reinforced PBT for injection molding applications.Information provided by Polyram. |
|||
| Melt Flow | 16.5 g/10 min @Load 1.20 kg, Temperature 300 °C |
16.5 g/10 min @Load 2.65 lb, Temperature 572 °F |
|
| Covestro Makrolon® T 7435 Polycarbonate, High Impact Impact modified injection molding grade, extremely easy flow and easy mold release, housings for portable mobile phones.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience wa.. |
|||
| Melt Flow | 16.5 g/10 min | 16.5 g/10 min | Condition G |
| Ineos Nova 3590 General Purpose Crystal Polystyrene
(discontinued **) Excellent blending resin, Suitable for difficult to fill and thin wall molding, Low residuals, USP Class VIApplications: Blending applications, Single service drinkware, Medical moldingExposure to g.. |
|||
| Melt Flow | 16.5 - 23.8 g/10 min | 16.5 - 23.8 g/10 min | Average value: 20.5 g/10 min Grade Count:5 |
| Overview of materials for Polybutylene Terephthalate (PBT), PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), PTFE Filled". Each property range of values reported is minimum and ma.. |
|||