Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 101 g/10 min @Load 5.00 kg, Temperature 270 °C |
101 g/10 min @Load 11.0 lb, Temperature 518 °F |
Estimated using room temperature density; ISO 1133 |
Lanxess Durethan® BKV 30 EF 000000 Nylon 6, 30% Glass Fiber PA 6, injection molding grade, 30% glass fibers, low viscosity (Easy Flow) |
|||
Melt Flow | 101 g/10 min @Load 5.00 kg, Temperature 270 °C |
101 g/10 min @Load 11.0 lb, Temperature 518 °F |
Estimated using room temperature density; ISO 1133 |
Lanxess Durethan® BKV 30 H2.0 EF 901510 Nylon 6, 30% Glass Fiber PA 6, 30% glass fibers, good flowability (Easy Flow), good heat-ageing resistance |
|||
Melt Flow | 101 g/10 min @Load 5.00 kg, Temperature 270 °C |
101 g/10 min @Load 11.0 lb, Temperature 518 °F |
Estimated using room temperature density; ISO 1133 |
Lanxess Durethan® BKV 30 H2.0 EF 900116 Nylon 6, 30% Glass Fiber PA 6, 30% glass fibers, good flowability (Easy Flow), good heat-ageing resistance |
|||
Melt Flow | 101 g/10 min @Load 2.16 kg, Temperature 230 °C |
101 g/10 min @Load 4.76 lb, Temperature 446 °F |
|
BASF Novolen® 1100 UC Polypropylene, Injection Molding Grade Injection molded partsData was collected by ISO methods and provided by BASF. |
|||
Melt Flow | 101 g/10 min @Load 2.16 kg, Temperature 230 °C |
101 g/10 min @Load 4.76 lb, Temperature 446 °F |
|
BASF Novolen® 1148 UC Polypropylene Nucleated grade with antistatic agent for injection molded parts.Data was collected by ISO methods and provided by BASF. |