Lanxess Durethan® BKV 30 H2.0 EF 901510 Nylon 6, 30% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® BKV 30 H2.0 EF 901510 Nylon 6, 30% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 6, 30% glass fibers, good flowability (Easy Flow), good heat-ageing resistance
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.600 g/cc | 0.0217 lb/in³ | ISO 60 |
| Density | 1.35 g/cc | 0.0488 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 2.1 % @Temperature 23.0 °C |
2.1 % @Temperature 73.4 °F |
50% RH; ISO 62 |
| Water Absorption at Saturation | 7.0 % @Temperature 23.0 °C |
7.0 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0029 cm/cm | 0.0029 in/in | 60x60x2; 280 °C / MT 80°C; 600 bar; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0081 cm/cm | 0.0081 in/in | 60x60x2; 280 °C / MT 80°C; 600 bar; ISO 294-4 |
| Melt Flow | 101 g/10 min @Load 5.00 kg, Temperature 270 °C |
101 g/10 min @Load 11.0 lb, Temperature 518 °F |
Estimated using room temperature density; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 193 MPa | 28000 psi | ISO 2039-1 |
| Tensile Strength at Break | 100 MPa | 14500 psi | Conditioned; ISO 527-1/-2 |
| 170 MPa | 24700 psi | ISO 527-1/-2 | |
| Elongation at Break | 3.2 % | 3.2 % | ISO 527-1/-2 |
| 5.8 % | 5.8 % | Conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 5.50 GPa | 798 ksi | Conditioned; ISO 527-1/-2 |
| 9.00 GPa | 1310 ksi | ISO 527-1/-2 | |
| Flexural Strength | 170 MPa | 24700 psi | Conditioned; ISO 178-A |
| 260 MPa | 37700 psi | ISO 178-A | |
| Flexural Yield Strength | 140 MPa | 20300 psi | at 3.5% strain; Conditioned; ISO 178-A |
| 255 MPa | 37000 psi | at 3.5% strain; ISO 178-A | |
| Flexural Modulus | 5.00 GPa | 725 ksi | Conditioned; ISO 178-A |
| 8.40 GPa | 1220 ksi | ISO 178-A | |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 180-1A |
| <= 10.0 kJ/m² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 180-1A | |
| 20.0 kJ/m² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 180-1A | |
| Izod Impact, Unnotched (ISO) | 50.0 kJ/m² @Temperature -30.0 °C |
23.8 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 180-1U |
| 55.0 kJ/m² @Temperature -30.0 °C |
26.2 ft-lb/in² @Temperature -22.0 °F |
ISO 180-1U | |
| 60.0 kJ/m² @Temperature 23.0 °C |
28.6 ft-lb/in² @Temperature 73.4 °F |
ISO 180-1U | |
| 75.0 kJ/m² @Temperature 23.0 °C |
35.7 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 180-1U | |
| Charpy Impact Unnotched | 5.50 J/cm² @Temperature -30.0 °C |
26.2 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 5.50 J/cm² @Temperature -30.0 °C |
26.2 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179/1eU | |
| 6.00 J/cm² @Temperature 23.0 °C |
28.6 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| 8.00 J/cm² @Temperature 23.0 °C |
38.1 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | 1.00 J/cm² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA | |
| 1.50 J/cm² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eA | |
| Impact | 803 | 803 | Puncture maximum force (N); ISO 6603-2 |
| 744 @Temperature -30.0 °C |
744 @Temperature -22.0 °F |
Puncture maximum force (N); ISO 6603-2 | |
| Puncture Energy | 2.10 J @Temperature -30.0 °C |
1.55 ft-lb @Temperature -22.0 °F |
ISO 6603-2 |
| 2.20 J @Temperature 23.0 °C |
1.62 ft-lb @Temperature 73.4 °F |
ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C | 11.1 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 100 µm/m-°C | 55.6 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1/-3 |
| Hot Ball Pressure Test | 210 °C | 410 °F | IEC 60695-10-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 150 °C | 302 °F | ISO 75-1/-2 |
| Vicat Softening Point | 210 °C | 410 °F | 120°C/hr; 50N; ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | Conditioned; IEC 60243-1 |
| 33.0 kV/mm | 838 kV/in | IEC 60243-1 | |
| Comparative Tracking Index | 400 V | 400 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 250 - 290 °C | 482 - 554 °F | Injection Molding |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | Injection Molding |
| Drying Temperature | 80.0 °C @Time 7200 - 22000 sec |
176 °F @Time 2.0 - 6.0 hour |
|
| Moisture Content | 0.03 - 0.12 % | 0.03 - 0.12 % | Karl Fischer method |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Release agent | |
| Form | Pellets | |
| ISO Shortname | ISO1874-PA6, MHR, 10-090, GF30 | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- Okulen® 1000 PE-UHMW, Natural
- Palm Labs Adhesives Turbo Anti-Seize Nickel Paste
- Mueller Ecostreamâ„¢ GreenDropâ„¢ C27451 DZR Lead Free Plumbing Brass
- Samsung Cheil Industries Starex® WR-9750 Extrusion Grade ABS
- SABIC Innovative Plastics NORYL GTX GTX987 PPE+PA66
- Chengdu Polyster 161 LPI Lenticular Lens Sheet, APET
- Carmel Olefins CAPILENE® SE 50 E Polypropylene Impact Copolymer
- Addiplast Addilene H 420 K24 Polypropylene Homopolymer
- Akzo Nobel Expancel® 051 DU 40 Dry unexpanded microspheres
Copyright © lookpolymers.com All Rights Reserved