Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 0.050 g/10 min | 0.050 g/10 min | ASTM D1238 |
Formosa Plastics Formolene® E905 Film HDPE
(discontinued **) HMW-Bimodal ResinApplications: T-shirt bags, trash can liners, heavy duty bagsFormolene E905 is a high molecular weight grade of HDPE with well-balanced strength in both the machine (MD) and transve.. |
|||
Melt Flow | 0.050 g/10 min @Load 2.16 kg |
0.050 g/10 min @Load 4.76 lb |
ISO 1133 |
SIDPEC EGYPTENE® HD 5301 FB HDPE Film Applications:Strong thin filmCarrier bagGrocery sacksFilm properties were measured on 15 micron film extruded at a blow up ratio of 5:1, 8D neck height.Information provided by Interchim s.r.l., offi.. |
|||
Melt Flow | 0.050 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.050 g/10 min @Load 4.76 lb, Temperature 374 °F |
Condition E; ASTM D1238 |
Formosa Plastics Formolene® E925 Film HDPE High Molecular Weight High Density Polyethylene (HMW-HDPE) for Film Extrusion Formolene® E925 is a bi-modal HMW-HDPE resin designed for high dart impact strength and good processing characteristics.. |
|||
Melt Flow | 0.050 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.050 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D-1238 |
Bapolene® 350F Polyethylene, Film Grade Applications: Blown film extrusion of T-shirt sacks, merchandise bags.Film properties below are based on a thickness of .8 mil and blow-up ratio of 4:1.Bapolene® and Bapolan® are registered tradem.. |