Polymer Property : Apparent Bulk Density = 0.560 g/cc Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Apparent Bulk Density	0.560 - 0.620 g/cc	0.0202 - 0.0224 lb/in³	Average value: 0.593 g/cc Grade Count:6
Overview of materials for Phenolic, Novolac, Woodflour Filled This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Novolac, Woodflour Filled". Each property range of values reported is minimum and maximum valu..
Apparent Bulk Density	0.560 g/cc	0.0202 lb/in³	ASTM D1895
Plenco 202 Black General Purpose Woodflour Filled Phenolic Molding Compound (discontinued **) Plaslok 202 is a two-stage, woodflour-filled phenolic molding compound formulated to provide improved impact and fatigue strength, good dimensional stability and excellent molded finish for automoti..
Apparent Bulk Density	0.560 g/cc	0.0202 lb/in³	ASTM D1895
Plaslok 202 Black General Purpose Woodflour Filled Phenolic Molding Compound (discontinued **) Plaslok Corporation was purchased by Plastics Engineering Company (maker of Plenco brand materials) in March 2000. The Plaslok name is no longer in use.Plaslok 202 is a two-stage, woodflour-filled ..
Apparent Bulk Density	0.560 g/cc	0.0202 lb/inÂ³	ASTM D1895
Solvay Specialty Polymers Catalyst CT/7 UV Polyolefin Catalyst CT/7 UV is a polyolefin based masterbatch to be used with cable silane crosslinkable compounds in the amount suggested for each material. Developed for PolidanÂ®, PolidiemmeÂ® and Cogeg..
Apparent Bulk Density	0.560 g/cc	0.0202 lb/inÂ³	ASTM D1895
Solvay Specialty Polymers Catalyst CT/7-LR UV Polyolefin Catalyst CT/7-LR UV is a polyolefin based masterbatch to be used with cable silane crosslinkable compounds in the amount suggested for each material. Developed for PolidanÂ®, PolidiemmeÂ® and Co..
Apparent Bulk Density	0.560 g/cc	0.0202 lb/inÂ³	ISO 1068
SolVin 173GB Polyvinyl Chloride Emulsion Polymer Made by emulsion polymerization. APPLICATIONS Calendering : plasticized films and sheets Extrusion : rigid or plasticized pipes and profiles In most cases, SolVin 173GB resin is used in blends with ..
Apparent Bulk Density	0.560 g/cc	0.0202 lb/inÂ³	Compacted; ISO 60
SolVin 178GI Polyvinyl Chloride General Purpose - Rigid Made by emulsion polymerization.APPLICATIONSCalendering : unplasticized PVC- film : Luvitherm processInformation provided by SolVin.
Apparent Bulk Density	0.560 g/cc	0.0202 lb/inÂ³	ISO 60
SolVin 260RF Polyvinyl Chloride General Purpose - Rigid Made by suspension polymerization. APPLICATIONS Extrusion : unplasticized PVC - tubes/pipes - profile - foam - sheet, film - blow moldings Calendering : unplasticized PVC - film : high temperature p..
Apparent Bulk Density	0.560 g/cc	0.0202 lb/in³	ASTM D792
Covestro Baydur® 730 IBS Polyurethane Structural Foam RIM, Density 35 pcf, MDI-based 2-Component Liquid System 0.25 in. thickness. IBS = Interactive Blowing System RIM = Reaction Injection MoldingInformation provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience ..
Apparent Bulk Density	0.560 g/cc	0.0202 lb/in³
Arkema Group Lacovyl® GB 1040 PVC LACOVYL GB 1040 is a medium molecular weight vinyl chloride homopolymer produced by mass polymerization process using the Elf Atochem's latest technology.Its characteristics are : Viscosity ind..