Polymer Property : Melt Index of Compound = 7.5 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Melt Index of Compound	7.5 g/10 min @Load 5.00 kg, Temperature 240 °C	7.5 g/10 min @Load 11.0 lb, Temperature 464 °F	ISO 1133
Polykemi AB SCANLON A 5005 PA/ABS-Blend Information provided by Polykemi AB
Melt Index of Compound	7.5 g/10 min @Load 5.00 kg, Temperature 240 °C	7.5 g/10 min @Load 11.0 lb, Temperature 464 °F	ISO 1133
Polykemi AB SCANLON A 5005B PA/ABS-Blend Information provided by Polykemi AB
Melt Index of Compound	7.5 g/10 min @Load 5.00 kg, Temperature 240 °C	7.5 g/10 min @Load 11.0 lb, Temperature 464 °F	ISO 1133
Polykemi AB SCANLON A 5005B UV PA/ABS-Blend Information provided by Polykemi AB
Melt Index of Compound	7.5 g/10 min @Load 5.00 kg, Temperature 200 °C	7.5 g/10 min @Load 11.0 lb, Temperature 392 °F	ASTM D1238G
Total Finaclear® 520 Clear Impact Polystyrene (discontinued **) Finaclear® 520 is a clear high styrenic styrene-butadiene (SBS) elastomer, providing dramatically improved impact properties and tear resistance to finished articles. Complemented by inherent repr..
Melt Index of Compound	7.5 g/10 min @Load 5.00 kg, Temperature 200 °C	7.5 g/10 min @Load 11.0 lb, Temperature 392 °F	ASTM D1238G
Total Finaclear® 521 Clear Impact Polystyrene (discontinued **) Finaclear® 521 is a clear high styrenic styrene-butadiene (SBS) elastomer, providing dramatically improved impact properties and tear resistance to finished articles, when used in blends with othe..
Melt Index of Compound	7.5 g/10 min	7.5 g/10 min	ASTM D1238
Dow AFFINITY™ PT 1450G1 Ethylene alpha-olefin resin AFFINITY™ PT 1450G1 Polyolefin Plastomer (POP) is produced via INSITE™ Technologies. The resin is for monolayer and co-extrusion coating that offers excellent low temperature seal initiation, ult..
Melt Index of Compound	7.5 g/10 min @Load 5.00 kg, Temperature 372 °C	7.5 g/10 min @Load 11.0 lb, Temperature 702 °F	ASTM D1238
3M Dyneon™ FEP 6307 R2RZ Fluorinated Ethylene Propylene Fluorothermoplastic Granules Dyneon FEP 6307 R2RZ is a special version of Dyneon FEP 6307 wire jacketing grade FEP with an added nucleating agent for improved foaming in gas injection extrusion processes. As the gas expands and..