Polymer Property : Linear Mold Shrinkage, Transverse = 0.025 cm/cm Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Linear Mold Shrinkage, Transverse	0.025 cm/cm	0.025 in/in	STN 64 0808
Plastcom SLOVALEN PC 53 N Polypropylene Copolymer, UV Stabilization FeaturesModified copolymer PP for injection moulding, with the ability of modeling the melt flow rate within the interval 5 - 20 g/10 min. Can be used for simple small as well as for large complica..
Linear Mold Shrinkage, Transverse	0.025 cm/cm	0.025 in/in	SABIC Method
SABIC Innovative Plastics LNP LUBRICOMP KL004L Acetal Copoly (Asia Pacific) LNP* Lubricomp* KL004L is a compound based on Acetal Copolymer resin containing PTFE. Added features of this material include: Internally Lubricated, Low Extractible.
Linear Mold Shrinkage, Transverse	0.025 cm/cm @Time 86400 sec	0.025 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP KL004L Acetal Copoly (Asia Pacific) LNP* Lubricomp* KL004L is a compound based on Acetal Copolymer resin containing PTFE. Added features of this material include: Internally Lubricated, Low Extractible.
Linear Mold Shrinkage, Transverse	0.025 - 0.027 cm/cm @Time 86400 sec	0.025 - 0.027 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP WX07423H PBT Health care grade, PTFE and silicone lubricated
Linear Mold Shrinkage, Transverse	0.025 - 0.027 cm/cm @Time 86400 sec	0.025 - 0.027 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRILOY KL201 Acetal LNP LUBRILOY* KL201 is a compound based on Acetal resin containing Proprietary Lubricant. PTFE. Added feature of this material is: Wear Resistant.
Linear Mold Shrinkage, Transverse	0.025 - 0.027 cm/cm @Time 86400 sec	0.025 - 0.027 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRILOY KL201 Acetal (Asia Pacific) LNP LUBRILOY* KL201 is a compound based on Acetal resin containing PTFE, Proprietary Lubricant. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Transverse	0.025 - 0.027 cm/cm @Time 86400 sec	0.025 - 0.027 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRILOY KL201 Acetal (Europe-Africa-Middle East) LNP LUBRILOY* KL201 is a compound based on Acetal resin containing PTFE, Proprietary Lubricant. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Transverse	0.025 - 0.030 cm/cm @Thickness 3.20 mm	0.025 - 0.030 in/in @Thickness 0.126 in	SABIC Method
SABIC Innovative Plastics ValoxÂ® V2105U PBT Unreinforced, Wear resistant, UV Stabilized PBT designed for outdoor, agricultural, industrial and automotive applications. This grade has very high impact strength to stiffness ratio.
Linear Mold Shrinkage, Transverse	0.025 - 0.030 cm/cm @Thickness 3.20 mm	0.025 - 0.030 in/in @Thickness 0.126 in	SABIC Method
SABIC Innovative Plastics ValoxÂ® V2105U PBT (Europe-Africa-Middle East) Unreinforced, Wear resistant, UV Stabilized PBT designed for outdoor, agricultural, industrial and automotive applications. This grade has very high impact strength to stiffness ratio.
Linear Mold Shrinkage, Transverse	0.025 cm/cm	0.025 in/in	ASTM D955
Teknor Apex MonpreneÂ® MP 1213A Thermoplastic Elastomer Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Fo..
Linear Mold Shrinkage, Transverse	0.025 - 0.030 cm/cm @Thickness 3.20 mm	0.025 - 0.030 in/in @Thickness 0.126 in	SABIC Method
SABIC Innovative Plastics Valox® V2105U PBT (Asia Pacific) Unreinforced, Wear resistant, UV Stabilized PBT designed for outdoor, agricultural, industrial and automotive applications. This grade has very high impact strength to stiffness ratio.