- Polymer Property : Linear Mold Shrinkage, Transverse = 0.016 in/in
Polymer Property : Linear Mold Shrinkage, Transverse = 0.016 in/in Product List
Physical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Linear Mold Shrinkage, Transverse | 0.014 - 0.016 cm/cm @Time 86400 sec |
0.014 - 0.016 in/in @Time 24.0 hour |
ASTM D 955 |
| SABIC Innovative Plastics LNP Lubricomp KCL22 Acetal Copoly (Asia Pacific) LNP* Lubricomp* KCL22 is a compound based on Acetal Copolymer resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated, Electrically Conductive.This data .. |
|||
| Linear Mold Shrinkage, Transverse | 0.014 - 0.016 cm/cm @Time 86400 sec |
0.014 - 0.016 in/in @Time 24.0 hour |
ASTM D955 |
| SABIC Innovative Plastics LNP LUBRICOMP WFL369 PBT LNP* Lubricomp* WFL369 is a compound based on Polybutylene Terephalate resin containing Glass Fiber, PTFE, Flame Retardant. Added features of this material include: Internally Lubricated, Flame Ret.. |
|||
| Linear Mold Shrinkage, Transverse | 0.014 - 0.016 cm/cm @Time 86400 sec |
0.014 - 0.016 in/in @Time 24.0 hour |
ASTM D955 |
| SABIC Innovative Plastics LNP LUBRICOMP WFL369 PBT (Asia Pacific) LNP* Lubricomp* WFL369 is a compound based on Polybutylene Terephalate resin containing Glass Fiber, PTFE, Flame Retardant. Added features of this material include: Internally Lubricated, Flame Ret.. |
|||
| Linear Mold Shrinkage, Transverse | 0.012 - 0.016 cm/cm @Thickness 2.30 - 4.60 mm |
0.012 - 0.016 in/in @Thickness 0.0906 - 0.181 in |
SABIC Method |
| SABIC Innovative Plastics Valox® 357 PBT PC/PBT, Unreinforced, impact modified, UL94V-0 rated. Applications like bobbins, switches and enclosures.This data was supplied by SABIC-IP for the Americas region. |
|||
| Linear Mold Shrinkage, Transverse | 0.012 - 0.016 cm/cm @Thickness 2.30 - 4.60 mm |
0.012 - 0.016 in/in @Thickness 0.0906 - 0.181 in |
SABIC Method |
| SABIC Innovative Plastics Valox® 357 PBT (Asia Pacific) PBT + PC, Unreinforced, impact modified, UL94V-0 rated. Applications like bobbins, switches and enclosures. |
|||
| Linear Mold Shrinkage, Transverse | 0.012 - 0.016 cm/cm @Thickness 2.30 - 4.60 mm |
0.012 - 0.016 in/in @Thickness 0.0906 - 0.181 in |
SABIC Method |
| SABIC Innovative Plastics Valox® 357 PBT+PC PC/PBT, Unreinforced, impact modified, UL94V-0 rated. Applications like bobbins, switches and enclosures. |
|||
| Linear Mold Shrinkage, Transverse | 0.012 - 0.016 cm/cm @Thickness 2.30 - 4.60 mm |
0.012 - 0.016 in/in @Thickness 0.0906 - 0.181 in |
SABIC Method |
| SABIC Innovative Plastics Valox® 357U PBT Unreinforced PBTP, UL94 V-0/5VA rated. Improved UV resistant version of VALOX 357. Nonblooming flame retardant.This data was supplied by SABIC-IP for the Americas region. |
|||
| Linear Mold Shrinkage, Transverse | 0.012 - 0.016 cm/cm @Thickness 2.30 - 4.60 mm |
0.012 - 0.016 in/in @Thickness 0.0906 - 0.181 in |
SABIC Method |
| SABIC Innovative Plastics Valox® 357U PBT (Asia Pacific) Unreinforced PBTP, UL94 V-0/5VA rated. Improved UV resistant version of VALOX 357. Nonblooming flame retardant. |
|||
| Linear Mold Shrinkage, Transverse | 0.012 - 0.016 cm/cm @Thickness 2.30 - 4.60 mm |
0.012 - 0.016 in/in @Thickness 0.0906 - 0.181 in |
SABIC Method |
| SABIC Innovative Plastics Valox® 365 PC+PET Unreinforced, opaque, provides chemical resistance and dimensional stability, UL94V-0 rated at 0.031"". |
|||
| Linear Mold Shrinkage, Transverse | 0.012 - 0.016 cm/cm @Thickness 2.30 - 4.60 mm |
0.012 - 0.016 in/in @Thickness 0.0906 - 0.181 in |
SABIC Method |
| SABIC Innovative Plastics Valox® 365 PET (Asia Pacific) Unreinforced, opaque, provides chemical resistance and dimensional stability, UL94V-0 rated at 0.031"". |
|||
| Linear Mold Shrinkage, Transverse | 0.013 - 0.016 cm/cm @Time 86400 sec |
0.013 - 0.016 in/in @Time 24.0 hour |
ASTM D955 |
| SABIC Innovative Plastics LNP STAT-KON MD000 PP LNP STAT-KON* MD000 is a compound based on Polypropylene resin containing Carbon Powder. Added feature of this material is: Electrically Conductive. |
|||
| Linear Mold Shrinkage, Transverse | 0.013 - 0.016 cm/cm @Time 86400 sec |
0.013 - 0.016 in/in @Time 24.0 hour |
ASTM D955 |
| SABIC Innovative Plastics LNP STAT-KON MD000 PP (Asia Pacific) LNP STAT-KON* MD000 is a compound based on Polypropylene resin containing Carbon Powder. Added features of this material include: Electrically Conductive. |
|||
| Linear Mold Shrinkage, Transverse | 0.012 - 0.016 cm/cm @Thickness 2.30 - 4.60 mm |
0.012 - 0.016 in/in @Thickness 0.0906 - 0.181 in |
SABIC Method |
| SABIC Innovative Plastics Xenoy® X3108UV PBT+PC (Europe-Africa-Middle East) Unreinforced, UV-stabilized, flame retardant, impact modified PBT+PC with V0 at 0.8mm thickness. For interior and exterior applications like wall switches and electrical enclosures.This data was sup.. |
|||
| Linear Mold Shrinkage, Transverse | 0.014 - 0.016 cm/cm @Time 86400 sec |
0.014 - 0.016 in/in @Time 24.0 hour |
ASTM D955 |
| SABIC Innovative Plastics LNP STAT-KON RFD02 PA 66 LNP* STAT-KON* RFD02 is a compound based on Nylon 66 resin containing 10% Glass Fiber. Added features of this material include: Electrically Conductive. |
|||
| Linear Mold Shrinkage, Transverse | 0.014 - 0.016 cm/cm @Time 86400 sec |
0.014 - 0.016 in/in @Time 24.0 hour |
ASTM D955 |
| SABIC Innovative Plastics LNP STAT-KON RFD02 PA 66 (Asia Pacific) LNP* Stat-kon* RFD02 is a compound based on Nylon 66 resin containing Glass Fiber, Carbon Powder. Added features of this material include: Electrically Conductive. |
|||
| Linear Mold Shrinkage, Transverse | 0.014 - 0.016 cm/cm @Time 86400 sec |
0.014 - 0.016 in/in @Time 24.0 hour |
ASTM D 955 |
| SABIC Innovative Plastics LNP Thermocomp IFB33 PA 6/12 LNP* Thermocomp* IFB33 is a compound based on Nylon 6/12 resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region. |
|||
| Linear Mold Shrinkage, Transverse | 0.014 - 0.016 cm/cm @Time 86400 sec |
0.014 - 0.016 in/in @Time 24.0 hour |
ASTM D 955 |
| SABIC Innovative Plastics LNP Thermocomp IFB33 PA 6/12 (Asia Pacific) LNP* Thermocomp* IFB33 is a compound based on Nylon 6/12 resin containing Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Linear Mold Shrinkage, Transverse | 0.014 - 0.016 cm/cm @Time 86400 sec |
0.014 - 0.016 in/in @Time 24.0 hour |
ASTM D955 |
| SABIC Innovative Plastics LNP THERMOCOMP MH0500C PP (Asia Pacific) LNP* Thermocomp* MH0500C is a compound based on Polypropylene resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity. |
|||
| Linear Mold Shrinkage, Transverse | 0.014 - 0.016 cm/cm @Time 86400 sec |
0.014 - 0.016 in/in @Time 24.0 hour |
ASTM D955 |
| SABIC Innovative Plastics LNP THERMOCOMP RF006H PA 66 LNP THERMOCOMP* RF006H is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added feature of this grade is: Healthcare. |
|||
| Linear Mold Shrinkage, Transverse | 0.014 - 0.016 cm/cm @Time 86400 sec |
0.014 - 0.016 in/in @Time 24.0 hour |
ISO 294 |
| SABIC Innovative Plastics LNP THERMOCOMP RF006H PA 66 LNP THERMOCOMP* RF006H is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added feature of this grade is: Healthcare. |
|||
| Linear Mold Shrinkage, Transverse | 0.014 - 0.016 cm/cm @Time 86400 sec |
0.014 - 0.016 in/in @Time 24.0 hour |
ASTM D955 |
| SABIC Innovative Plastics LNP THERMOCOMP RF006XXZ PA 66 LNP THERMOCOMP* RF006XXZ is a compound based on Nylon 66 resin containing 30% Glass Fiber |
|||
| Linear Mold Shrinkage, Transverse | 0.014 - 0.016 cm/cm @Time 86400 sec |
0.014 - 0.016 in/in @Time 24.0 hour |
ISO 294 |
| SABIC Innovative Plastics LNP THERMOCOMP RF006XXZ PA 66 LNP THERMOCOMP* RF006XXZ is a compound based on Nylon 66 resin containing 30% Glass Fiber |
|||
| Linear Mold Shrinkage, Transverse | 0.014 - 0.016 cm/cm @Time 86400 sec |
0.014 - 0.016 in/in @Time 24.0 hour |
ASTM D 955 |
| SABIC Innovative Plastics LNP Lubricomp KCL22 Acetal Copoly LNP* Lubricomp* KCL22 is a compound based on Acetal Copolymer resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated, Electrically Conductive.This data .. |
|||
| Linear Mold Shrinkage, Transverse | 0.012 - 0.016 cm/cm @Thickness 2.30 - 4.60 mm |
0.012 - 0.016 in/in @Thickness 0.0906 - 0.181 in |
SABIC Method |
| SABIC Innovative Plastics Valox® 357U PBT+PC Unreinforced PC/PBT, UL94 V-0/5VA rated. Improved UV resistant version of VALOX 357. Nonblooming flame retardant. |
|||
| Linear Mold Shrinkage, Transverse | 0.012 - 0.016 cm/cm @Thickness 2.30 - 4.60 mm |
0.012 - 0.016 in/in @Thickness 0.0906 - 0.181 in |
SABIC Method |
| SABIC Innovative Plastics Valox® 365 PET Unreinforced, opaque, provides chemical resistance and dimensional stability, UL94V-0 rated at 0.031".This data was supplied by SABIC-IP for the Americas region. |
|||
| Linear Mold Shrinkage, Transverse | 0.012 - 0.016 cm/cm @Thickness 2.30 - 4.60 mm |
0.012 - 0.016 in/in @Thickness 0.0906 - 0.181 in |
SABIC Method |
| SABIC Innovative Plastics Xenoy® X3108UV PBT+PC (Asia Pacific) Unreinforced, UV-stabilized, flame retardant, impact modified PBT+PC with V0 at 0.8mm thickness. For interior and exterior applications like wall switches and electrical enclosures.This data was sup.. |
|||
| Linear Mold Shrinkage, Transverse | 0.014 - 0.016 cm/cm @Time 86400 sec |
0.014 - 0.016 in/in @Time 24.0 hour |
ASTM D955 |
| SABIC Innovative Plastics LNP THERMOCOMP MH0500C PP LNP* THERMOCOMP* MH0500C is a compound based on Polypropylene resin. Added feature of this material is: High Specific Gravity. |
|||