SABIC Innovative Plastics LNP LUBRICOMP WFL369 PBT

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP WFL369 PBT.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp* WFL369 is a compound based on Polybutylene Terephalate resin containing Glass Fiber, PTFE, Flame Retardant. Added features of this material include: Internally Lubricated, Flame Retardant.
Physical Properties Metric English Comments
Density 1.78 g/cc
0.0643 lb/in³
ASTM D792
1.78 g/cc
0.0643 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm

@Time 86400 sec
0.0040 - 0.0060 in/in

@Time 24.0 hour
ASTM D955
0.0051 cm/cm

@Time 86400 sec
0.0051 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.015 cm/cm

@Time 86400 sec
0.015 in/in

@Time 24.0 hour
ISO 294
0.014 - 0.016 cm/cm

@Time 86400 sec
0.014 - 0.016 in/in

@Time 24.0 hour
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 102 MPa
14800 psi
ASTM D638
106 MPa
15400 psi
ISO 527
Tensile Strength, Yield 105 MPa
15200 psi
ASTM D638
106 MPa
15400 psi
ISO 527
Elongation at Break 2.0 %
2.0 %
ISO 527
2.1 %
2.1 %
ASTM D638
Elongation at Yield 2.0 %
2.0 %
ISO 527
2.1 %
2.1 %
ASTM D638
Tensile Modulus 11.2 GPa
1620 ksi
1 mm/min; ISO 527
12.41 GPa
1800 ksi
50 mm/min; ASTM D638
Flexural Strength 158 MPa
22900 psi
ASTM D790
161 MPa
23400 psi
ISO 178
Flexural Modulus 8.90 GPa
1290 ksi
ISO 178
10.34 GPa
1500 ksi
ASTM D790
Izod Impact, Notched 0.580 J/cm
1.09 ft-lb/in
ASTM D256
Izod Impact, Unnotched 6.67 J/cm
12.5 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 37.0 kJ/m²
17.6 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 6.00 J
4.43 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 2.00 J
1.48 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.53
0.53
ASTM D3702 Modified
Coefficient of Friction, Static 0.41
0.41
ASTM D3702 Modified
K (wear) Factor 50.4 x 10-8 mm³/N-M
25.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 70.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
38.9 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
70.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
39.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 28.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
16.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
29.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
16.1 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 221 °C
430 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
221 °C

@Thickness 3.20 mm
430 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 207 °C
405 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
207 °C

@Thickness 3.20 mm
405 °F

@Thickness 0.126 in
unannealed; ASTM D648
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
UL 94 by SABIC-IP