Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 8.30 - 8.40 g/cc | 0.300 - 0.303 lb/in³ | |
Kennametal Stellite Denertiaâ„¢ C13 Cobalt Chromium Dental Alloy Denertiaâ„¢ C13 is a cobalt chromium base-metal casting alloy for the manufacture of removable partial dentures and bridgework.This alloy is Nickel, Beryllium and Cadmium free as defined in ISO 6.. |
|||
Density | 8.30 - 8.40 g/cc | 0.300 - 0.303 lb/in³ | |
Kennametal Stellite Denertia™ C14 Cobalt Chromium Dental Alloy Denertia™ C14 is a cobalt chromium base-metal casting alloy for the manufacture of removable partial dentures and bridgework. It conforms to the following International Standards: EN 1641 §.. |
|||
Density | 8.30 g/cc | 0.300 lb/in³ | |
Materion BrushCAST® 20C High Strength Casting Alloy (As Cast & Aged) Pouring Temperature: 1010-1120°CHeat treatment required for max strength (Annealing): 760-790°C/water quenchHeat treatment required for max strength (Hardening): 760-790°C/water quenchDescr.. |
|||
Density | 8.30 g/cc | 0.300 lb/in³ | |
Materion BrushCAST® 20C High Strength Casting Alloy (Solution Annealed & Aged) Pouring Temperature: 1010-1120°CHeat treatment required for max strength (Annealing): 760-790°C/water quenchHeat treatment required for max strength (Hardening): 760-790°C/water quenchDescr.. |
|||
Density | 8.30 g/cc | 0.300 lb/in³ | |
Materion BrushCAST® 21C High Strength Casting Alloy (Solution Annealed & Aged) Pouring Temperature: 1010-1120°CHeat treatment required for max strength (Annealing): 760-790°C/water quenchHeat treatment required for max strength (Hardening): 760-790°C/water quenchDescr.. |
|||
Density | 8.30 g/cc | 0.300 lb/in³ | |
Materion BrushCAST® 20CT Fine Grain Casting Alloy (As Cast & Aged) Pouring Temperature: 1010-1120°CHeat treatment required for max strength (Annealing): 760-790°C/water quenchHeat treatment required for max strength (Hardening): 760-790°C/water quenchDescr.. |
|||
Density | 8.30 g/cc | 0.300 lb/in³ | |
Special Metals INCONEL® 725 Nickel Superalloy (UNS N07725) Age Hardened Strip Tensile strength (ultimate and yield), hardness, impact, and elongation values reported here are typical for Age Hardened Strip samples. Other property values are typical of INCONEL® alloy 725.D.. |
|||
Density | 8.30 g/cc | 0.300 lb/in³ | |
Special Metals INCONEL® 725 Nickel Superalloy (UNS N07725), Age Hardened Round Tensile strength (ultimate and yield), hardness, impact, and elongation values reported here are typical for Age Hardened Round samples. Other property values are typical of INCONEL® alloy 725.D.. |
|||
Density | 8.30 g/cc | 0.300 lb/in³ | |
Special Metals INCONEL® 725 Nickel Superalloy (UNS N07725), Age Hardened Tube Tensile strength (ultimate and yield), hardness, and elongation values reported here are typical for Age Hardened Tube samples. Other property values are typical of INCONEL® alloy 725.Data provi.. |
|||
Density | 8.30 g/cc | 0.300 lb/in³ | |
Special Metals INCONEL® Alloy MA 754 A mechanically alloyed nickel-chromium alloy with oxide dispersion strengthening. Mechanical alloying, which involves high-energy milling of metal powders, is used to create a uniformly distributed.. |
|||
Density | 8.30 g/cc | 0.300 lb/in³ | |
Goodfellow Havar® High-Strength Non-Magnetic Cobalt-Base Alloy Co42.5/Cr20/Ni13/Fe/W/Mo/MnInformation provided by Goodfellow. |
|||
Density | 8.30 g/cc | 0.300 lb/in³ | |
Elgiloy® Co-Cr-Ni Alloy, Strip General Elgiloy® information: High strength, ductility, fatigue life, and good mechanical properties. Corrosion resistant in numerous environments. Available in strip (currently 0.0015" to 0.075".. |
|||
Density | 8.30 g/cc | 0.300 lb/in³ | |
Elgiloy® Co-Cr-Ni Alloy, Strip, 20% Cold Reduction, Heat Treated Heat Treatment 5 hours at 482°C. The strength, elongation, and hardness values are specific to this heat treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High .. |
|||
Density | 8.30 g/cc | 0.300 lb/in³ | |
Elgiloy® Co-Cr-Ni Alloy, Strip, 30% Cold Reduction The strength, elongation, and hardness values are specific to this cold reduction treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High strength, ductility, fati.. |
|||
Density | 8.30 g/cc | 0.300 lb/in³ | |
Elgiloy® Co-Cr-Ni Alloy, Strip, 40% Cold Reduction The strength, elongation, and hardness values are specific to this cold reduction treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High strength, ductility, fati.. |
|||
Density | 8.30 g/cc | 0.300 lb/in³ | |
Elgiloy® Co-Cr-Ni Alloy, Strip, 50% Cold Reduction The strength, elongation, and hardness values are specific to this cold reduction treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High strength, ductility, fati.. |
|||
Density | 8.30 g/cc | 0.300 lb/in³ | |
Elgiloy® Co-Cr-Ni Alloy, Strip, 65% Cold Reduction, Heat Treated Heat Treatment 5 hours at 482°C. The strength, elongation, and hardness values are specific to this heat treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High .. |
|||
Density | 8.30 g/cc | 0.300 lb/in³ | |
Elgiloy® Co-Cr-Ni Alloy, Wire, 30% Cold Reduction, Heat Treated Heat Treatment 5 hours at 527°C. The strength, shear modulus, and hardness values are specific to this heat treatment; other values below are typical of Elgiloy®.General Elgiloy® information: Hi.. |
|||
Density | 8.30 g/cc | 0.300 lb/in³ | |
Elgiloy® Co-Cr-Ni Alloy, Strip, 10% Cold Reduction, Heat Treated Heat Treatment 5 hours at 482°C. The strength, elongation, and hardness values are specific to this heat treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High .. |
|||
Density | 8.30 g/cc | 0.300 lb/in³ | |
Elgiloy® Co-Cr-Ni Alloy, Wire, 20% Cold Reduction The strength, shear modulus, and hardness values are specific to this cold reduction treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High strength, ductility, f.. |
|||
Density | 8.30 g/cc | 0.300 lb/in³ | |
Elgiloy® Co-Cr-Ni Alloy, Wire, 40% Cold Reduction The strength, shear modulus, and hardness values are specific to this cold reduction treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High strength, ductility, f.. |
|||
Density | 8.30 g/cc | 0.300 lb/in³ | |
Elgiloy® Co-Cr-Ni Alloy, Wire, 40% Cold Reduction, Heat Treated Heat Treatment 5 hours at 527°C. The strength, shear modulus, and hardness values are specific to this heat treatment; other values below are typical of Elgiloy®.General Elgiloy® information: Hi.. |
|||
Density | 8.30 g/cc | 0.300 lb/in³ | |
Elgiloy® Co-Cr-Ni Alloy, Wire, 65% Cold Reduction The strength, shear modulus, and hardness values are specific to this cold reduction treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High strength, ductility, f.. |
|||
Density | 8.30 g/cc | 0.300 lb/in³ | |
Bohler-Uddeholm BÖHLER S400(M7) High Speed Steel Description: High alloyed molybdenum high speed steel with good resistance and high toughness.Applications: Taps, twist drills, reamers, milling tools, broaches tools, cold extrusion dies.Standards:.. |
|||
Density | 8.30 g/cc | 0.300 lb/in³ | |
ATI Allvac® Nickelvac® TJA-1537™ UNS R31537 & UNS R31538 Nickel Superalloy Cobalt-base alloy for machined and forged medical and surgical devices requiring high fatigue strength; total joint replacement.Property values are for samples in the metallurgical condition: Warm w.. |
|||
Density | 8.30 g/cc | 0.300 lb/in³ | |
ATI Allvac® Nickelvac® X-750 Nickel Superalloy, Heat Treatment: 1149°C (2100°F) + Age Data provided by Allvac.Applications: Turbine, engine components. Blades, vanes, fasteners, springs, bellows. Extrusion dies, nuclear, heat treating, forming tools. |
|||
Density | 8.30 g/cc | 0.300 lb/in³ | |
ATI Allvac® Nickelvac® X-750 Nickel Superalloy, Heat Treatment: 982°C (1800°F) + Age Data provided by Allvac.Applications: Turbine, engine components. Blades, vanes, fasteners, springs, bellows. Extrusion dies, nuclear, heat treating, forming tools. |