Vyncolit X6952 Novolac Phenolic

Category	Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic , Phenolic, Novolac, Glass Filled
Manufacturer	Vyncolit N.V., Sumitomo Bakelite
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Vyncolit X6952 Novolac Phenolic.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Glass fiber reinforced phenolic molding compound with superior mechanical properties: very high tensile and flexural strength combined with high elongation at break.USES: Information provided by Vyncolit, a Sumitomo Bak Group

Physical Properties	Metric	English	Comments
Bulk Density	0.650 g/cc	0.0235 lb/in³	Powder Density; ISO 60
Density	1.70 g/cc	0.0614 lb/in³	Relative Density; ISO 1183
Linear Mold Shrinkage	0.0017 cm/cm	0.0017 in/in	Injection Molding; ISO 2577

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	130 MPa	18900 psi	ISO 527
Elongation at Break	1.0 %	1.0 %	Tensile; ISO 527
	1.6 %	1.6 %	Flexure; ISO 178
Tensile Modulus	20.0 GPa	2900 ksi	ISO 527
Flexural Strength	250 MPa	36300 psi	At Rupture; ISO 178
Flexural Modulus	17.5 GPa	2540 ksi	ISO 178
Compressive Strength	280 MPa	40600 psi	ISO 604
Charpy Impact Unnotched	2.10 J/cm²	9.99 ft-lb/in²	ISO 179
Charpy Impact, Notched	0.500 J/cm²	2.38 ft-lb/in²	ISO 179

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	20.0 µm/m-°C @Temperature 20.0 °C	11.1 µin/in-°F @Temperature 68.0 °F	TMA
CTE, linear, Transverse to Flow	30.0 µm/m-°C @Temperature 20.0 °C	16.7 µin/in-°F @Temperature 68.0 °F	TMA
Deflection Temperature at 1.8 MPa (264 psi)	220 °C	428 °F	ISO 75 Af
Flammability, UL94	V-0 @Thickness 1.60 mm	V-0 @Thickness 0.0630 in
	V-0 @Thickness 4.00 mm	V-0 @Thickness 0.157 in
Shrinkage	0.020 %	0.020 %	Post Shrinkage; ISO 2577

Electrical Properties	Metric	English	Comments
Volume Resistivity	4.00e+12 ohm-cm	4.00e+12 ohm-cm	DIN 53482
Surface Resistance	7.00e+12 ohm	7.00e+12 ohm	IEC 93
Insulation Resistance	1.00e+11 ohm	1.00e+11 ohm	Wet; 24 hours in water; IEC 167
	1.00e+12 ohm	1.00e+12 ohm	Dry; IEC 167
Dielectric Strength	30.0 kV/mm	762 kV/in	IEC 243
Comparative Tracking Index	175 V	175 V	IEC 112

Descriptive Properties	Value	Comments
Color	Green
ISO type	PF 2 C3
Main Filler	Glass Fiber
Molding Method	Compression, transfer, injection