- Victrex® PEEK 90HMF40 Polyetheretherketone (PEEK), 40% Carbon Fiber Reinforced
Victrex® PEEK 90HMF40 Polyetheretherketone (PEEK), 40% Carbon Fiber Reinforced
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Carbon Fiber Filled |
| Manufacturer | Victrex |
| Trade Name | PEEK |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Victrex® PEEK 90HMF40 Polyetheretherketone (PEEK), 40% Carbon Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: High performance thermoplastic material, 40% carbon fiber reinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection molding, easy flow, color black.Typical Application Areas: Complex geometries with thinner cross sections or longer flow length where superior strength in a static or dynamic system is required. Excellent wear resistance, low coefficient of friction, low coefficient of thermal expansion. Chemically resistant to aggressive environments.All information provided by Victrex.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.45 g/cc @Temperature 23.0 °C |
1.45 g/cc @Temperature 73.4 °F |
Crystalline; ISO 1183 |
| Water Absorption at Saturation | 0.30 % @Temperature 23.0 °C |
0.30 % @Temperature 73.4 °F |
immersion; ISO 62-1 |
| 0.40 % @Temperature 100 °C |
0.40 % @Temperature 212 °F |
immersion; ISO 62-1 | |
| Viscosity | 300000 cP @Temperature 400 °C |
300000 cP @Temperature 752 °F |
melt; ISO 11443 |
| Linear Mold Shrinkage, Flow | 0.00 cm/cm | 0.00 in/in | 380°C nozzle, 190°C tool; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0040 cm/cm | 0.0040 in/in | 380°C nozzle, 190°C tool; ISO 294-4 |
| Spiral Flow | 10.0 cm @Thickness 1.00 mm |
3.94 in @Thickness 0.0394 in |
380°C nozzle, 190°C tool |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 88.5 | 88.5 | ISO 868 |
| Tensile Strength at Break | 85.0 MPa @Temperature 275 °C |
12300 psi @Temperature 527 °F |
ISO 527 |
| 145 MPa @Temperature 180 °C |
21000 psi @Temperature 356 °F |
ISO 527 | |
| 220 MPa @Temperature 120 °C |
31900 psi @Temperature 248 °F |
ISO 527 | |
| 330 MPa @Temperature 23.0 °C |
47900 psi @Temperature 73.4 °F |
ISO 527 | |
| Elongation at Yield | 1.2 % @Temperature 23.0 °C |
1.2 % @Temperature 73.4 °F |
ISO 527 |
| Tensile Modulus | 43.0 GPa @Temperature 23.0 °C |
6240 ksi @Temperature 73.4 °F |
ISO 527 |
| Flexural Strength | 120 MPa @Temperature 275 °C |
17400 psi @Temperature 527 °F |
ISO 178 |
| 220 MPa @Temperature 180 °C |
31900 psi @Temperature 356 °F |
ISO 178 | |
| 350 MPa @Temperature 120 °C |
50800 psi @Temperature 248 °F |
ISO 178 | |
| 475 MPa @Temperature 23.0 °C |
68900 psi @Temperature 73.4 °F |
ISO 178 | |
| Flexural Modulus | 37.0 GPa @Temperature 23.0 °C |
5370 ksi @Temperature 73.4 °F |
ISO 178 |
| Compressive Strength | 120 MPa @Temperature 200 °C |
17400 psi @Temperature 392 °F |
ISO 604 |
| 250 MPa @Temperature 120 °C |
36300 psi @Temperature 248 °F |
ISO 604 | |
| 310 MPa @Temperature 23.0 °C |
45000 psi @Temperature 73.4 °F |
ISO 604 | |
| Izod Impact, Notched (ISO) | 10.5 kJ/m² @Temperature 23.0 °C |
5.00 ft-lb/in² @Temperature 73.4 °F |
ISO 180 |
| Izod Impact, Unnotched (ISO) | 60.0 kJ/m² @Temperature 23.0 °C |
28.6 ft-lb/in² @Temperature 73.4 °F |
ISO 180 |
| Charpy Impact Unnotched | 6.00 J/cm² @Temperature 23.0 °C |
28.6 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1U |
| Charpy Impact, Notched | 0.800 J/cm² @Temperature 23.0 °C |
3.81 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 35.0 µm/m-°C @Temperature <=143 °C |
19.4 µin/in-°F @Temperature <=289 °F |
Average below Tg; ISO 11359 |
| 80.0 µm/m-°C @Temperature >=143 °C |
44.4 µin/in-°F @Temperature >=289 °F |
Average above Tg; ISO 11359 | |
| CTE, linear, Parallel to Flow | 1.00 µm/m-°C @Temperature >=143 °C |
0.556 µin/in-°F @Temperature >=289 °F |
Above Tg; ISO 11359 |
| 3.00 µm/m-°C @Temperature <=143 °C |
1.67 µin/in-°F @Temperature <=289 °F |
Below Tg; ISO 11359 | |
| Thermal Conductivity | 2.00 W/m-K | 13.9 BTU-in/hr-ft²-°F | Average; ISO 22007-4 |
| 4.30 W/m-K | 29.8 BTU-in/hr-ft²-°F | Along flow; ISO 22007-4 | |
| Melting Point | 343 °C | 649 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 349 °C | 660 °F | ISO 75A-f |
| Glass Transition Temp, Tg | 143 °C | 289 °F | Onset; ISO 11357 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1e+05 | 1e+05 | 1V; ASTM D4496 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | <= 100 °C | <= 212 °F | Hopper Temperature |
| Nozzle Temperature | 385 °C | 725 °F | |
| Mold Temperature | 190 - 200 °C | 374 - 392 °F | |
| Drying Temperature | >= 150 °C @Time 10800 sec |
>= 302 °F @Time 3.00 hour |
|
| >= 160 °C @Time 7200 sec |
>= 320 °F @Time 2.00 hour |
Users viewing this material also viewed the following:
- Parker Chomerics SOFT-SHIELD® 7000 Low Closure Force EMI Gasket
- Plastcom SLOVASTER® B GF 30 FRL 4 Polybutylene Terephthalate, 30% Chemically Coupled Glass Fiber, Bromine Hydrocarbon Flame Retardant
- Haynes 230® alloy, 20% cold reduction, 1177°C anneal for 5 minutes
- Special Metals Electroformed Nickel, 200 Micron (8 mil) Foil, Electroformed and Annealed
- Shin-Etsu Silicones KF-8017 Fluid
- Silberline Silvet® 440-20-P
- Sax Polymers SAXATEC 4307 Acrylonitrile Styrene Acrylate
- Chase Plastics CP Pryme® NN130GMD2HS (COND, 50% RH) Nylon 66, 30% Glass Fiber Reinforced, 2% MoS2 Lubricated, Heat Stabilized
- ATI Allegheny Ludlum 425 Mod Martensitic Stainless Steel
- ExxonMobil Santoprene® 8271-80HT Thermoplastic Rubber (discontinued **)
Copyright © lookpolymers.com All Rights Reserved