Techmer ES Luriblend® PSU TL20
| Category | Polymer , Thermoplastic , Polysulfone (PSU) , Polysulfone with PTFE/Silicone Filler |
| Manufacturer | Techmer ES |
| Trade Name | Luriblend® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Luriblend® PSU TL20.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsAdditive: PTFE LubricantFeatures: LubricatedInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ASTM D792 |
| Water Absorption | 0.14 % @Time 86400 sec |
0.14 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0070 cm/cm @Thickness 3.17 mm |
0.0070 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 68 | 68 | ASTM D785 |
| Tensile Strength, Yield | 52.4 MPa | 7600 psi | ASTM D638 |
| Elongation at Break | 25 % | 25 % | ASTM D638 |
| Flexural Yield Strength | 81.4 MPa | 11800 psi | ASTM D790 |
| Flexural Modulus | 2.62 GPa | 380 ksi | ASTM D790 |
| Izod Impact, Notched | 0.854 J/cm @Thickness 3.17 mm |
1.60 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 61.2 µm/m-°C | 34.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 188 °C | 370 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 350 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | ASTM D257 |
| Dielectric Strength | 19.7 kV/mm | 500 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- Plastcom SLOVALEN PC 78 FRD 1 Polypropylene Copolymer, Halogen Flame Retardant, UV Stabilized
- Inno-Comp INNOPOL® CS 3-3120 B 20% Talc-Filled Polypropylene
- Haynes 556® alloy, bar, after 4000 hours at 650°C (1200°F)
- Solvay TECHNYL® A 218 V35 Black 34 NG PA66, 35% glass fiber, DRY
- SABIC Innovative Plastics Valox® V4860HR PBT (Europe-Africa-Middle East)
- A. Schulman POLYBATCH™ Yellow 2600V Concentrate Based In Polyethylene
- Eastman Tenite 307E0V16310 Propionate Clear, Trsp
- Fainplast Compounds PG 80 Flexible PVC, Extrusion Modified with Rubber
- STAR Thermoplastic Alloys & Rubbers StarFlex® P 7335-9000 TPE
- Lucite International SW Sanitary Ware Acrylic Sheet
Copyright © lookpolymers.com All Rights Reserved