Victrex® PEEK 90G Polyetheretherketone, Unreinforced

Category Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Unreinforced
Manufacturer Victrex
Trade Name PEEK
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Victrex® PEEK 90G Polyetheretherketone, Unreinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description:High performance thermoplastic material, unreinforced Polyetheretherketone (PEEK), semi crystalline, depth filtered granules for injection moulding, easy flow, FDA food contact compliant, colour natural/beige.Typical Application Areas:Complex geometries with thinner cross sections or longer flow lengths, for high strength and stiffness as well as good ductility. Chemically resistant to aggressive environments, suitable for sterilization for medical and food contact applications.Information Provided by VICTREX®
Physical Properties Metric English Comments
Density 1.30 g/cc
0.0470 lb/in³
Crystalline; ISO 1183
Water Absorption at Saturation 0.40 %

@Temperature 23.0 °C
 0.40 %

@Temperature 73.4 °F
 Equilibrium; by immersion; ISO 62-1
0.55 %

@Temperature 100 °C
 0.55 %

@Temperature 212 °F
 immersion; ISO 62-1
Viscosity 90000 cP

@Temperature 400 °C
 90000 cP

@Temperature 752 °F
 melt; ISO 11443
Linear Mold Shrinkage, Flow 0.010 cm/cm
0.010 in/in
360°C nozzle, 160°C tool; ISO 294-4
Linear Mold Shrinkage, Transverse 0.013 cm/cm
0.013 in/in
360°C nozzle, 160°C tool; ISO 294-4
Spiral Flow 24.5 cm

@Thickness 1.00 mm
 9.65 in

@Thickness 0.0394 in
 365°C nozzle, 160°C tool
28.0 cm

@Thickness 1.00 mm
 11.0 in

@Thickness 0.0394 in
 375°C nozzle, 180°C tool
33.0 cm

@Thickness 1.00 mm
 13.0 in

@Thickness 0.0394 in
 400°C nozzle, 200°C tool
Mechanical Properties Metric English Comments
Hardness, Shore D 85

@Temperature 23.0 °C
 85

@Temperature 73.4 °F
 ISO 868
Tensile Strength, Yield 105 MPa

@Temperature 23.0 °C
 15200 psi

@Temperature 73.4 °F
 ISO 527
Elongation at Break 20 %

@Temperature 23.0 °C
 20 %

@Temperature 73.4 °F
 ISO 527
Tensile Modulus 4.10 GPa

@Temperature 23.0 °C
 595 ksi

@Temperature 73.4 °F
 ISO 527
Flexural Strength 13.5 MPa

@Temperature 275 °C
 1960 psi

@Temperature 527 °F
 ISO 178
20.0 MPa

@Temperature 175 °C
 2900 psi

@Temperature 347 °F
 ISO 178
90.0 MPa

@Temperature 125 °C
 13100 psi

@Temperature 257 °F
 ISO 178
175 MPa

@Temperature 23.0 °C
 25400 psi

@Temperature 73.4 °F
 ISO 178
130 MPa

@Strain 3.50 %,
Temperature 23.0 °C
 18900 psi

@Strain 3.50 %,
Temperature 73.4 °F
 ISO 178
Flexural Modulus 3.90 GPa

@Temperature 23.0 °C
 566 ksi

@Temperature 73.4 °F
 ISO 178
Compressive Strength 80.0 MPa

@Temperature 120 °C
 11600 psi

@Temperature 248 °F
 ISO 604
130 MPa

@Temperature 23.0 °C
 18900 psi

@Temperature 73.4 °F
 ISO 604
Izod Impact, Notched (ISO) 4.50 kJ/m²

@Temperature 23.0 °C
 2.14 ft-lb/in²

@Temperature 73.4 °F
 ISO 180/A
Izod Impact, Unnotched (ISO) NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 ISO 180/U
Charpy Impact Unnotched NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 ISO 180/U
Charpy Impact, Notched 0.450 J/cm²

@Temperature 23.0 °C
 2.14 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear 55.0 µm/m-°C

@Temperature <=143 °C
 30.6 µin/in-°F

@Temperature <=289 °F
 Average below Tg; ISO 11359
140 µm/m-°C

@Temperature >=143 °C
 77.8 µin/in-°F

@Temperature >=289 °F
 Average above Tg; ISO 11359
CTE, linear, Parallel to Flow 50.0 µm/m-°C

@Temperature <=143 °C
 27.8 µin/in-°F

@Temperature <=289 °F
 Below Tg; ISO 11359
120 µm/m-°C

@Temperature >=143 °C
 66.7 µin/in-°F

@Temperature >=289 °F
 Above Tg; ISO 11359
Thermal Conductivity 0.320 W/m-K
2.22 BTU-in/hr-ft²-°F
Along flow; ISO 22007-4
0.290 W/m-K

@Temperature 23.0 °C
 2.01 BTU-in/hr-ft²-°F

@Temperature 73.4 °F
 Average; ISO/CD 22007-4
Melting Point 343 °C
649 °F
ISO 11357
Deflection Temperature at 1.8 MPa (264 psi) 156 °C
313 °F
As molded; ISO 75A-f
167 °C

@Temperature 200 °C,
Time 14400 sec
 333 °F

@Temperature 392 °F,
Time 4.00 hour
 Annealed; ISO 75A-f
Glass Transition Temp, Tg 143 °C
289 °F
Onset; ISO 11357
Oxygen Index 24 %

@Thickness 0.400 mm
 24 %

@Thickness 0.0157 in
 ISO 4239
35 %

@Thickness 3.20 mm
 35 %

@Thickness 0.126 in
 ISO 4239
Glow Wire Test 960 °C

@Thickness 2.00 mm
 1760 °F

@Thickness 0.0787 in
 IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+9 ohm-cm

@Temperature 275 °C
 1.00e+9 ohm-cm

@Temperature 527 °F
 IEC 60093
1.00e+15 ohm-cm

@Temperature 125 °C
 1.00e+15 ohm-cm

@Temperature 257 °F
 IEC 60093
1.00e+16 ohm-cm

@Temperature 23.0 °C
 1.00e+16 ohm-cm

@Temperature 73.4 °F
 IEC 60093
Dielectric Constant 3.1

@Frequency 1000 Hz,
Temperature 23.0 °C
 3.1

@Frequency 1000 Hz,
Temperature 73.4 °F
 IEC 60250
Dielectric Strength 23.0 kV/mm

@Thickness 2.50 mm
 584 kV/in

@Thickness 0.0984 in
 IEC 60243-1
Dissipation Factor 0.0040

@Frequency 1.00e+6 Hz,
Temperature 23.0 °C
 0.0040

@Frequency 1.00e+6 Hz,
Temperature 73.4 °F
 IEC 60250
Comparative Tracking Index 150 V
150 V
IEC 60112
Processing Properties Metric English Comments
Mold Temperature 170 - 200 °C
338 - 392 °F
Drying Temperature 120 °C

@Time 18000 sec
 248 °F

@Time 5.00 hour
150 °C

@Time 10800 sec
 302 °F

@Time 3.00 hour
Descriptive Properties Value Comments
Toxicity Index 0.074
NES 713; CO content
0.15
NES 713; CO<sub>2</sub> content
0.22
NES 713; Total gases