SABIC Innovative Plastics LNP LUBRICOMP OCL36 PPS - Linear (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port, China
Download PDF SABIC Innovative Plastics LNP LUBRICOMP OCL36 PPS - Linear (Europe-Africa-Middle East).pdf
Price EMAIL US  sales@lookpolymers.com
Material Notes:
LNP* Lubricomp* OCL4036L is a compound based on PPS - Linear resin containing PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive.
Mechanical Properties Metric English Comments
Density 1.57 g/cc
0.0567 lb/in³
ISO 1183
Thermal Properties Metric English Comments
Tensile Strength at Break 163 MPa
23600 psi
5 mm/min; ISO 527
Elongation at Break 0.80 %
0.80 %
5 mm/min; ISO 527
Tensile Modulus 24.9 GPa
3610 ksi
1 mm/min; ISO 527
Flexural Strength 219 MPa
31800 psi
2 mm/min; ISO 178
Flexural Modulus 21.3 GPa
3090 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 25.0 kJ/m²
11.9 ft-lb/in²
80*10*4; ISO 180/1U
Optical Properties Metric English Comments
CTE, linear, Parallel to Flow 3.00 µm/m-°C
<br>@Temperature 23.0 - 60.0 °C
 1.67 µin/in-°F
<br>@Temperature 73.4 - 140 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 55.0 µm/m-°C
<br>@Temperature 23.0 - 60.0 °C
 30.6 µin/in-°F
<br>@Temperature 73.4 - 140 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 258 °C
496 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi) 278 °C
532 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
Chemical Resistance Properties Metric English Comments
Surface Resistance 10 - 1000 ohm
10 ohm
ASTM D257