Victrex® PEEK 150GL15 Polyetheretherketone, 15% Glass Fibre Reinforced

Category Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Glass Fiber Filled
Manufacturer Victrex
Trade Name PEEK
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Victrex® PEEK 150GL15 Polyetheretherketone, 15% Glass Fibre Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description:High performance thermoplastic material, 15% glass fibre reinforced Polyetheretherketone (PEEK), semi crystalline, granules for injection moulding, very easy flow, FDA food contact compliant, colour natural/beige.Typical Application Areas:Complex geometries with thin cross sections or long flow lengths where good strength in a static or dynamic system is required. Low coefficient of thermal expansion. Chemically resistant to aggressive environments, suitable for sterilization for medical and food contact applications.Information Provided by VICTREX®
Physical Properties Metric English Comments
Density 1.40 g/cc
0.0506 lb/in³
Crystalline; ISO 1183
Water Absorption at Saturation 0.40 %

@Temperature 23.0 °C
0.40 %

@Temperature 73.4 °F
Equilibrium; by immersion; ISO 62-1
0.50 %

@Temperature 100 °C
0.50 %

@Temperature 212 °F
immersion; ISO 62-1
Viscosity 200000 cP

@Temperature 400 °C
200000 cP

@Temperature 752 °F
melt; ISO 11443
Linear Mold Shrinkage, Flow 0.0040 cm/cm
0.0040 in/in
360°C nozzle, 160°C tool; ISO 294-4
Linear Mold Shrinkage, Transverse 0.010 cm/cm
0.010 in/in
375°C nozzle, 180°C tool; ISO 294-4
Spiral Flow 18.0 cm

@Thickness 1.00 mm
7.09 in

@Thickness 0.0394 in
375°C nozzle, 180°C tool
Mechanical Properties Metric English Comments
Hardness, Shore D 86

@Temperature 23.0 °C
86

@Temperature 73.4 °F
ISO 868
Tensile Strength at Break 135 MPa

@Temperature 23.0 °C
19600 psi

@Temperature 73.4 °F
ISO 527
Elongation at Break 2.4 %

@Temperature 23.0 °C
2.4 %

@Temperature 73.4 °F
ISO 527
Tensile Modulus 7.50 GPa

@Temperature 23.0 °C
1090 ksi

@Temperature 73.4 °F
ISO 527
Flexural Strength 215 MPa

@Temperature 23.0 °C
31200 psi

@Temperature 73.4 °F
ISO 178
Flexural Modulus 7.30 GPa

@Temperature 23.0 °C
1060 ksi

@Temperature 73.4 °F
ISO 178
Izod Impact, Notched (ISO) 0.600 kJ/m²

@Temperature 23.0 °C
0.286 ft-lb/in²

@Temperature 73.4 °F
ISO 180/A
Izod Impact, Unnotched (ISO) 2.50 kJ/m²

@Temperature 23.0 °C
1.19 ft-lb/in²

@Temperature 73.4 °F
ISO 180/U
Thermal Properties Metric English Comments
CTE, linear 55.0 µm/m-°C

@Temperature <=143 °C
30.6 µin/in-°F

@Temperature <=289 °F
Average below Tg; ISO 11359
120 µm/m-°C

@Temperature >=143 °C
66.7 µin/in-°F

@Temperature >=289 °F
Average above Tg; ISO 11359
CTE, linear, Parallel to Flow 30.0 µm/m-°C

@Temperature <=143 °C
16.7 µin/in-°F

@Temperature <=289 °F
Below Tg; ISO 11359
30.0 µm/m-°C

@Temperature >=143 °C
16.7 µin/in-°F

@Temperature >=289 °F
Above Tg; ISO 11359
Thermal Conductivity 0.300 W/m-K
2.08 BTU-in/hr-ft²-°F
Average; ISO 22007-4
0.350 W/m-K

@Temperature 23.0 °C
2.43 BTU-in/hr-ft²-°F

@Temperature 73.4 °F
Along flow; ISO/CD 22007-4
Melting Point 343 °C
649 °F
ISO 11357
Deflection Temperature at 1.8 MPa (264 psi) 323 °C
613 °F
ISO 75-f
Glass Transition Temp, Tg 143 °C
289 °F
Onset; ISO 11357
147 °C
297 °F
Midpoint; ISO 11357
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
IEC 60093
Dielectric Strength 23.0 kV/mm

@Thickness 50.8 mm
584 kV/in

@Thickness 2.00 in
IEC 30243-1
Comparative Tracking Index 150 V
150 V
IEC 60093
Processing Properties Metric English Comments
Processing Temperature <= 100 °C
<= 212 °F
Hopper Temperature
Nozzle Temperature 375 °C
707 °F
Mold Temperature 170 - 200 °C
338 - 392 °F
Drying Temperature 120 °C

@Time 18000 sec
248 °F

@Time 5.00 hour
150 °C

@Time 10800 sec
302 °F

@Time 3.00 hour