Unitika TERRAMAC TE-1070 Polylactic Acid (PLA)
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Polylactic Acid (PLA) Biopolymer |
| Manufacturer | Unitika |
| Trade Name | TERRAMAC |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Unitika TERRAMAC TE-1070 Polylactic Acid (PLA).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High-Impact grade, Injection grade. Bio-based materials produced from annually renewable raw materials.Information provided by Unitika Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 34.0 MPa | 4930 psi | ISO 527 |
| Elongation at Break | >= 200 % | >= 200 % | ISO 527 |
| Flexural Strength | 50.0 MPa | 7250 psi | ISO 178 |
| Flexural Modulus | 1.40 GPa | 203 ksi | ISO 178 |
| Charpy Impact, Notched | 0.560 J/cm² | 2.66 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 170 °C | 338 °F | |
| Maximum Service Temperature, Air | 240 °C | 464 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 54.0 °C | 129 °F | ISO 75 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 130 - 170 °C | 266 - 338 °F | |
| Middle Barrel Temperature | 180 - 220 °C | 356 - 428 °F | |
| Front Barrel Temperature | 180 - 220 °C | 356 - 428 °F | |
| Nozzle Temperature | 180 - 220 °C | 356 - 428 °F | |
| Mold Temperature | 10.0 - 30.0 °C | 50.0 - 86.0 °F | actual surface temp |
| Back Pressure | 0.490 - 1.47 MPa | 71.1 - 213 psi | gage pressure |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Opaque white |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® D 5308 HF Black TPO Thermoplastic Polyolefin Elastomer
- Lehmann & Voss ELECTRAFIL M-2386 Polycarbonate, with carbon fiber and PTFE
- SABIC Innovative Plastics LNP Stat-loy AX06484X ABS
- UBE 7034T Nylon 6/12 Monofilament (Drawing Ratio=5, Diameter 0.4 mm)
- Polyplastics Freqtis® C0711A (PPS/LCP), Molding Compound
- Covestro Makrolon® 2407 Polycarbonate, Injection Grade
- DuPont Performance Polymers VESPEL TP-8130 Polyimide
- ConocoPhillips Hydroclear® 2 Ultra-clean multi-purpose R&O Oil, AGMA Lubricant No. 2
- 3M AC-251 Gray Class B-2 Aerospace Sealant
- Solvay Specialty Polymers Amodel® AF-1145 V0 Polyphthalamide (PPA) Resin, 45% Glass Reinforced, at 50% RH (di
Copyright © lookpolymers.com All Rights Reserved