Unitika M1030DH PA6, Dry
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | Unitika |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Unitika M1030DH PA6, Dry.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nano composite nylonInformation provided by Unitika Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ISO 1183 |
| Water Absorption | 0.90 % @Time 86400 sec |
0.90 % @Time 24.0 hour |
ISO 62 |
| Moisture Absorption at Equilibrium | 2.8 % | 2.8 % | 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0080 cm/cm @Thickness 3.20 mm |
0.0080 in/in @Thickness 0.126 in |
|
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm @Thickness 3.20 mm |
0.010 in/in @Thickness 0.126 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 114 | 114 | ISO 2039 |
| Tensile Strength at Break | 95.0 MPa | 13800 psi | ISO 527-1/-2 |
| Elongation at Break | 3.4 % | 3.4 % | ISO 527-1/-2 |
| Tensile Modulus | 4.30 GPa | 624 ksi | ISO 527-1/-2 |
| Flexural Strength | 155 MPa | 22500 psi | ISO 178 |
| Flexural Modulus | 4.50 GPa | 653 ksi | ISO 178 |
| Izod Impact, Notched | 0.450 J/cm | 0.843 ft-lb/in | ASTM D256 |
| Charpy Impact Unnotched | 5.70 J/cm² | 27.1 ft-lb/in² | ISO 179-1 |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | ISO 179-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 53.0 µm/m-°C | 29.4 µin/in-°F | ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 186 °C | 367 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | ISO 75-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 |
| Dielectric Constant | 3.7 @Frequency 1.00e+6 Hz |
3.7 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dielectric Strength | 42.1 kV/mm @Thickness 1.00 mm |
1070 kV/in @Thickness 0.0394 in |
IEC 60243-1 |
| Dissipation Factor | 0.019 @Frequency 1.00e+6 Hz |
0.019 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Arc Resistance | 122 sec | 122 sec | ASTM D495 |
| Comparative Tracking Index | 475 V | 475 V | IEC 60112 |
Users viewing this material also viewed the following:
- Overview of materials for Polypropylene, Molded
- Heatbath/Park #90 Casing Salt for Liquid Nitriding
- Samsung Cheil Industries Starex® ES-0173 ABS, Extrusion Grade
- Techmer ES HiFill® HDPE
- Plenco 7507 Phenolic, Granular, Transfer Molded
- Zeon Chemicals Hydrin® C2000LL Polyepichlorohydrin Elastomer
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 0.50 PHR Zinc Stearate
- Vyncolit BXE7670 Glass Filled Phenolic Molding Compound
- ExxonMobil PP1014H1 Polypropylene Homopolymer
- Fainplast Compounds FAINGUM 6530 Flexible PVC, Injection Molding for Footwear
Copyright © lookpolymers.com All Rights Reserved