- Unitika BV2120G30 PA66, 30% Glass Fiber Reinforced, Flame Retardant, Conditioned
Unitika BV2120G30 PA66, 30% Glass Fiber Reinforced, Flame Retardant, Conditioned
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Unitika |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Unitika BV2120G30 PA66, 30% Glass Fiber Reinforced, Flame Retardant, Conditioned.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Unitika Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.65 g/cc | 0.0596 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.90 % | 0.90 % | 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Thickness 3.20 mm |
0.0030 in/in @Thickness 0.126 in |
|
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm @Thickness 3.20 mm |
0.0070 in/in @Thickness 0.126 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 102 | 102 | ISO 2039 |
| Tensile Strength at Break | 113 MPa | 16400 psi | ISO 527-1/-2 |
| Elongation at Break | 2.3 % | 2.3 % | ISO 527-1/-2 |
| Tensile Modulus | 8.70 GPa | 1260 ksi | ISO 527-1/-2 |
| Flexural Strength | 170 MPa | 24700 psi | ISO 178 |
| Flexural Modulus | 8.20 GPa | 1190 ksi | ISO 178 |
| Charpy Impact Unnotched | 5.00 J/cm² | 23.8 ft-lb/in² | ISO 179-1 |
| Charpy Impact, Notched | 1.10 J/cm² | 5.23 ft-lb/in² | ISO 179-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 30.0 µm/m-°C | 16.7 µin/in-°F | ISO 11359-2 |
| Flammability, UL94 | V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
Users viewing this material also viewed the following:
- Polimeri Europa Greenflex® FF 45 Ethylene Vinyl Acetate Copolymer - Blown Film Extrusion
- Nilit FRIANYL A63 HH-SG-GV 2020 Nylon 6.6 for injection molding, 20% mineral filled, 20% glass fiber reinforced
- Huntsman Matrimid 5292A Resin
- Shuman FR380 Grey PC/ABS Alloy, Flame Retardant
- Styron CALIBREâ„¢ 301-15 Polycarbonate Resin
- DuPont Elvaloy® 1125 AC Ethylene and 25% Methyl Acrylate Copolymer
- A. Schulman SCHULAMID® 6 MV14 Unreinforced Nylon 6
- Formosa Plastics Formolene® L42022E2 Film (Butene Grade) LLDPE
- CPC - Vycom FLAMETEC™ CPVC Chlorinated Polyvinyl Chloride Sheet
Copyright © lookpolymers.com All Rights Reserved