Unitika A175G15 PA66, 15% Glass Fiber Reinforced, Conditioned
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled |
| Manufacturer | Unitika |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Unitika A175G15 PA66, 15% Glass Fiber Reinforced, Conditioned.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Unitika Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.26 g/cc | 0.0455 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 1.9 % | 1.9 % | 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm @Thickness 3.20 mm |
0.0060 in/in @Thickness 0.126 in |
|
| Linear Mold Shrinkage, Transverse | 0.015 cm/cm @Thickness 3.20 mm |
0.015 in/in @Thickness 0.126 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 73.0 MPa | 10600 psi | ISO 527-1/-2 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527-1/-2 |
| Tensile Modulus | 3.50 GPa | 508 ksi | ISO 527-1/-2 |
| Flexural Strength | 110 MPa | 16000 psi | ISO 178 |
| Flexural Modulus | 3.20 GPa | 464 ksi | ISO 178 |
| Charpy Impact Unnotched | 3.90 J/cm² | 18.6 ft-lb/in² | ISO 179-1 |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | ISO 179-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 42.0 µm/m-°C | 23.3 µin/in-°F | ISO 11359-2 |
| Flammability, UL94 | HB @Thickness 0.840 mm |
HB @Thickness 0.0331 in |
Users viewing this material also viewed the following:
- Osprey Metals 90/10 Cu Sn Powder (Grade 80% - 22)
- LG Chemical NBR 3280 High Acrylonitrile Polymer
- Heatbath/Park #3 Granular Charcoal Pack Carburizing Compound
- LyondellBasell Higlass SB224-1 Polypropylene Copolymer, 10% Glass Fiber
- SABIC Innovative Plastics LNP LUBRICOMP RFL46ES PA 66
- Shakespeare Isocorâ„¢ TT25TI Nylon 6 Terpolymer
- A. Schulman POLYFORT™ PP 1329 UV Stabilized, Medium Impact Copolymer Polypropylene
- Dow Corning SILASTIC® FL 40-9201 A&B KIT
- ExxonMobil Exceed™ 2018CA Metallocene Polyethylene Resin (European Grade)
- Arlon Thermabond® 48991A010 0.010" (0.254 mm) Uncured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved