Unitika A1025GO PA6, Flame Retardant, Conditioned
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced, Flame Retardant |
| Manufacturer | Unitika |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Unitika A1025GO PA6, Flame Retardant, Conditioned.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Unitika Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.64 g/cc | 0.0592 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 1.0 % | 1.0 % | 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Thickness 3.20 mm |
0.0020 in/in @Thickness 0.126 in |
|
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm @Thickness 3.20 mm |
0.0070 in/in @Thickness 0.126 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 102 | 102 | ISO 2039 |
| Tensile Strength at Break | 110 MPa | 16000 psi | ISO 527-1/-2 |
| Elongation at Break | 2.5 % | 2.5 % | ISO 527-1/-2 |
| Tensile Modulus | 7.00 GPa | 1020 ksi | ISO 527-1/-2 |
| Flexural Strength | 140 MPa | 20300 psi | ISO 178 |
| Flexural Modulus | 6.00 GPa | 870 ksi | ISO 178 |
| Charpy Impact Unnotched | 3.10 J/cm² | 14.8 ft-lb/in² | ISO 179-1 |
| Charpy Impact, Notched | 1.40 J/cm² | 6.66 ft-lb/in² | ISO 179-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 30.0 µm/m-°C | 16.7 µin/in-°F | ISO 11359-2 |
| Flammability, UL94 | V-0 @Thickness 0.870 mm |
V-0 @Thickness 0.0343 in |
Users viewing this material also viewed the following:
- Nylacast POM C Acetal Copolymer
- M Chemical GUARD DOGâ„¢ UV9 Light Stabilizer, Benzophenone Derivative
- Lucas-Milhaupt AL 719 Aluminum Brazing Filler Metal
- SABIC Innovative Plastics NORYL 731S PPE+HIPS (Europe-Africa-Middle East)
- A. Schulman POLYBATCH™ Green 3011E Concentrate Based In Polyethylene
- Teknor Apex Vidux® CV-1000-88 Polyvinyl Chloride, Flexible
- Dow Corning Z-1229 TETRACHLOROSILANE
- CP-Polymer-Technik Wellamid® 6600 MZ 401 CP Combination Nylon 66, Conditioned
- Chosun Refractories FSS95 Flame-Gunning Repair Refractory
- A. Schulman POLYFORT™ PP 1329 UV Stabilized, Medium Impact Copolymer Polypropylene
Copyright © lookpolymers.com All Rights Reserved