Unipetrol PP MONSTEN® GB 503 Polypropylene Impact Copolymer
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | Unipetrol RPA |
| Trade Name | PP MONSTEN® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Unipetrol PP MONSTEN® GB 503 Polypropylene Impact Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Made for injection molding applications. Basic stabilization. Impact copolymer.Information provided by Unipetrol RPA
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
3.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ISO 527 |
| Elongation at Break | >= 200 % | >= 200 % | ISO 527 |
| Flexural Modulus | 1.25 GPa | 181 ksi | ISO 178 |
| Charpy Impact, Notched | 0.700 J/cm² @Temperature -20.0 °C |
3.33 ft-lb/in² @Temperature -4.00 °F |
ISO 179 |
| 6.00 J/cm² @Temperature 23.0 °C |
28.6 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | ISO 75 |
| Vicat Softening Point | 150 °C | 302 °F | ISO 306 |
Users viewing this material also viewed the following:
- Polimersan Plastics POLITEF® (PTFE) with 25% Carbon
- Gouda Vuurvast CURASBOND 85 Moldable Refractory Material
- LG Chemical LUPOY GP-2301F General Purpose Modified PC, 30% Glass Fiber Reinforced, Flame Retardant
- Karina 837-35/1-E-ERYB Ivory PVC Compound
- Solvay Specialty Polymers solvene® T 2808 Electroactive Polymer (EAP)
- Techmer ES HiFill® PA6/6 GF33 BK024 33% Glass Filled (Conditioned)
- Shin-Etsu Silicones KF-6005 Fluid
- 3M 4605 Silicone Rubber Termination Kit
Copyright © lookpolymers.com All Rights Reserved