- UBE UBEPOL BR150 Non-Oil Extended Synthetic Rubber Vulcanizate (Cured 50 Minutes at 145°C)
UBE UBEPOL BR150 Non-Oil Extended Synthetic Rubber Vulcanizate (Cured 50 Minutes at 145°C)
| Category | Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | UBE |
| Trade Name | UBEPOL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | UBE UBEPOL BR150 Non-Oil Extended Synthetic Rubber Vulcanizate (Cured 50 Minutes at 145°C).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: UBEPOL BR is UBE's line of polybutadiene rubber products.Information provided by UBE.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 62 | 62 | ASTM D412 |
| Tensile Strength at Break | 18.0 MPa | 2610 psi | ASTM D412 |
| Elongation at Break | 480 % | 480 % | ASTM D412 |
| 100% Modulus | 0.00220 GPa | 0.319 ksi | ASTM D412 |
| 200% Modulus | 0.00540 GPa | 0.783 ksi | ASTM D412 |
| 300% Modulus | 0.0100 GPa | 1.45 ksi | ASTM D412 |
| Rebound | 58 % | 58 % | BS.903,PART22 |
| Tear Strength | 47.0 kN/m | 268 pli | ASTM D624 |
| Abrasion | 100 | 100 | Lombourn Abrasion Index (Iwamoto Seisakusyo, Japan); UBE Method |
| 209 | 209 | Pico Abrasion Index; ASTM D2228 | |
| Compression Set | 16 % | 16 % | Method B, 70°C, 72hrs; ASTM D395 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Cut Generation De Mattia Flexing Machine | Min 300,000 times | ASTM D430 |
| Cut Growth (2mm-->15mm) De Mattia Flexing Machine | 2700 times | ASTM D313 |
| Goodrich Flex, 0.175" Stroke, 55lb, 100°C, P.S. | 8% | ASTM D623 (32°C change in temperature) |
| Wet Skid Resistance on Safety-Walk | 18 | UBE Method (British Portable Skid Resistance Tester) |
Users viewing this material also viewed the following:
- Pau Tai UNISTAB RP-33K Solid Complex Stabilizer
- SABIC Innovative Plastics Lexan® HF1130 PC
- Solvay Specialty Polymers Ixef® 1501/0003 Polyarylamide, 30% Glass Fiber, DAM (discontinued **)
- Michelman® DigiPrime® 6029 Primer
- Samsung Cheil Industries Infino® UF-1017S PC, Unreinforced FR
- Tra-Con Tra-Cast F353 Optically Opaque Casting System
- Teknor Apex Telcar® TL-2069B Thermoplastic Elastomer
- A. Schulman LP479-01 High-Density Polyethylene Homopolymer
- Covestro Makrolon® ET UV530 Polycarbonate
- PolyOne Lubri-Tech™ AM-30CF/15T Polyphthalamide (PPA), Carbon Fiber Reinforced, PTFE Lubricated (discontinued
Copyright © lookpolymers.com All Rights Reserved