- Diamond Polymers ABSPC 9901GF20 Injection Molding Grade, 20% Glass Filled
Diamond Polymers ABSPC 9901GF20 Injection Molding Grade, 20% Glass Filled
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Glass Fiber Filled , Polycarbonate (PC) |
| Manufacturer | Diamond and Network Polymers |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Diamond Polymers ABSPC 9901GF20 Injection Molding Grade, 20% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.27 g/cc | 1.27 g/cc | ASTM D792 |
| Melt Flow | 22 g/10 min @Load 5.00 kg, Temperature 265 °C |
22 g/10 min @Load 11.0 lb, Temperature 509 °F |
ASTM D1238 |
| Ash | 18 - 22 % | 18 - 22 % | ASTM D5630 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 74.1 MPa | 10700 psi | chs 2.0 in/min; ASTM D638 |
| Elongation at Break | 1.9 % | 1.9 % | chs 2.0 in/min; ASTM D638 |
| Flexural Strength | 109.6 MPa @Thickness 3.17 mm |
15900 psi @Thickness 0.125 in |
chs 0.05 in/min; ASTM D790 |
| Flexural Modulus | 4.823 GPa @Thickness 3.17 mm |
699.5 ksi @Thickness 0.125 in |
tangent; chs 0.05 in/min; ASTM D790 |
| Izod Impact, Notched | 0.801 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
1.50 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 137 °C @Load 1.00 kg, Thickness 3.17 mm |
279 °F @Load 2.20 lb, Thickness 0.125 in |
ASTM D1525 |
Users viewing this material also viewed the following:
- Nanocyl PLASTICYL™ PBT1501 Polybutylene Terephthalate - Carbon Nanotube Masterbatch
- NOVA Chemicals Novapol® PF-0218-J Butene LLDPE Film Resin
- Kostat ICP-STAT ICS-1005 ABS Sheet
- Grupo Repol Dinalon® A1S25 MI PA66 Medium Impact
- Silberline Silvex® 223-20-C
- Master Bond Supreme 33CLV Two Component, Room Temperature Curing Toughened Epoxy
- Carpenter MP35N* Ni-Co-Cr-Mo Alloy, 35% Cold Reduction + Aged 538°C (1000°F)/4hr/AC
- Asahi Kasei Leona® FG170 Nylon 66
- Ashley Polymers Ashlene® 63M Nylon 66, Mineral Filled
- Plaskolite West Optix® CA - 2000 High Impact Acrylic Resin
Copyright © lookpolymers.com All Rights Reserved